- 产 品：POM 511P NC010 中高粘度,热稳定,低翘曲
- 产 地：DuPont 杜邦
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
DuPont™ Delrin® 数据
杜邦™塑钢®
acetal resin
缩醛树脂
Unreinforced Resins
增强树脂
Delrin® 511P NC010 is a medium viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding(reduced warpage, less shrinkage, fewer voids).
塑钢®511p NC010 是中高粘度聚甲醛均聚物具有改进的热稳定性和修改为更精确成型（减少翘曲，不收缩，减少空隙）。
|
Property
|
Test Method
|
Units
|
Value
|
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
POM
>POM<
|
|
Mechanical
Yield Stress
Yield Strain
Strain at Break
Nominal Strain at Break
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Flexural Modulus
Flexural Stress
@ 3.5% Strain
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 899
ISO 178
ISO 178
|
MPa (kpsi)
%
%
%
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
|
73 (10.6)
12
35
25
3400 (490)
3000 (435)
1700 (247)
3100 (450)
90 (13.1)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Mechanical
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 179/1eA
ISO 179/1eU
|
2
kJ/m
2
kJ/m
|
7
8
220
260
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Parallel
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
Vicat Softening Temperature
50N
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
°C (°F)
|
165 (329)
107 (225)
178 (352)
0.96 (0.53)
1.1 (0.61)
1.30 (0.72)
0.96 (0.53)
1.1 (0.61)
1.47 (0.82)
160 (320)
|
|
Rheological
Melt Mass-Flow Rate
190°C, 2.16kg
Melt Volume-Flow Rate
|
ISO 1133
ISO 1133
|
g/10 min
3
cm /10 min (ml/10 min)
|
15
13
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Electrical
Surface Resistivity
Volume Resistivity
Relative Permittivity
1E2 Hz
1E6 Hz
Dissipation Factor
1E6 Hz
CTI
|
IEC 60093
IEC 60093
IEC 60250
IEC 60250
IEC 60112
|
ohm
ohm m
E-4
V
|
>1E15
1E12
3.5
3.8
60
600
|
|
Flammability
Flammability Classification
0.75mm
1.5mm
3.0mm
Oxygen Index
|
IEC 60695-11-10
ISO 4589-1/-2
|
%
|
HB
HB
HB
22
|
|
Temperature Index
RTI, Electrical
0.75mm
1.5mm
3.0mm
RTI, Impact
0.75mm
1.5mm
3.0mm
RTI, Strength
0.75mm
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
°C
°C
°C
|
50
110
110
50
85
90
50
90
95
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Other
Density
Hardness, Rockwell
Scale M
Scale R
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 2039/2
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m (g/cm )
%
%
|
1420 (1.42)
92
120
0.2
0.9
1.7
1.8
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
Hold Pressure Range
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
MPa (kpsi)
|
210-220 (410-430)
215 (420)
80-100 (175-210)
90 (195)
2-4
80 (175)
<0.2
80-100 (12-15)
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Delrin® are trademarks or registered trademarks of DuPont Company. Copyright© 2008