联系我们
- 产 品：POM 111P NC010 高粘度,热稳定,低翘曲
- 产 地：DuPont 杜邦
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
DuPont™ Delrin® 数据
杜邦™塑钢®
acetal resin
缩醛树脂
UV Resistant/Weatherable Resins
防紫外线/耐候性树脂
Delrin® 111P is a high viscosity acetal homopolymer with improved thermal stability and modifications for more precise moulding (reduced warpage, fewer voids). It has higher tensile strength and modulus than Delrin ® 100P.
塑钢®111p是高粘度聚甲醛均聚物具有改进的热稳定性和修改为更精确成型（减少翘曲，减少空隙）。它具有较高的拉伸强度和弹性模量比Delrin®100P。
|
Property
|
Test Method
|
Units
|
Value
|
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
POM
>POM<
|
|
Mechanical
Yield Stress
Yield Strain
Strain at Break
Nominal Strain at Break
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Flexural Modulus
Flexural Stress
@ 3.5% Strain
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 899
ISO 178
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
%
%
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
72 (10.4)
20
50
35
3200 (464)
3000 (435)
1700 (247)
2900 (420)
80 (11.6)
9
11
270
300
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
|
ISO 75-1/-2
|
°C (°F)
|
165 (329)
100 (212)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Thermal
Melting Temperature
10°C/min
CLTE, Parallel
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
Vicat Softening Temperature
50N
|
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
°C (°F)
|
178 (352)
0.94 (0.52)
1.0 (0.72)
1.3 (0.72)
0.94 (0.52)
1.1 (0.61)
1.4 (0.78)
160 (320)
|
|
Rheological
Melt Mass-Flow Rate
190°C, 2.16kg
|
ISO 1133
|
g/10 min
|
2.4
|
|
Electrical
CTI
|
IEC 60112
|
V
|
600
|
|
Flammability
Flammability Classification
1.5mm
3.0mm
Flammability Classification
1.5mm
Oxygen Index
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
|
%
|
HB
HB
HB
17
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Temperature Index
RTI, Electrical
1.5mm
3.0mm
RTI, Impact
1.5mm
3.0mm
RTI, Strength
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
°C
°C
°C
|
110
110
85
90
90
95
|
|
Other
Density
Hardness, Rockwell
Scale M
Scale R
Water Absorption
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 2039/2
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m (g/cm )
%
%
|
1420 (1.42)
92
120
1.0
1.9
2.1
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
Hold Pressure Range
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
MPa (kpsi)
|
210-220 (410-430)
215 (420)
80-100 (175-210)
90 (195)
2-4
80 (175)
<0.2
90-110 (13-16)
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Delrin® are trademarks or registered trademarks of DuPont Company. Copyright© 2006