DuPont Delrin®
杜邦塑钢®
acetal resin
缩醛树脂
Extrusion Resins
挤出树脂
Delrin® 100P is a high viscosity acetal homopolymer for use in easy to fill molds. Delrin® 100P provides maximum toughness in the product line without modification. Delrin ® 100P has improved processing thermal stability.
聚甲醛®100P是一种高粘度聚甲醛均聚物,容易使用,以填补模具。聚甲醛®100P提供了最大的韧性,在未经修改的产品线。聚甲醛®100P加工热稳定性有所改善。
Property
|
Test Method
|
Units
|
Value
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
POM
>POM<
|
Mechanical
Yield Stress
Yield Strain
Strain at Break
50mm/min
Nominal Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
%
%
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
71 (10.3)
22
50
35
3000 (435)
2800 (405)
10
11
300
|
Property
|
Test Method
|
Units
|
Value
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
CLTE, Parallel
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 100°C (130 - 212°F)
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
|
165 (330)
93 (200)
178 (350)
1.0 (0.56)
1.1 (0.6)
1.5 (0.83)
1.0 (0.56)
1.1 (0.6)
1.5 (0.83)
|
Rheological
Melt Mass-Flow Rate
190°C, 2.16kg
|
ISO 1133
|
g/10 min
|
2.5
|
Flammability
Flammability Classification
0.75mm
1.5mm
3.0mm
Flammability Classification
0.75mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
|
|
HB
HB
HB
HB
HB
HB
|
Property
|
Test Method
|
Units
|
Value
|
Temperature Index
RTI, Electrical
0.75mm
1.5mm
3.0mm
RTI, Impact
0.75mm
1.5mm
3.0mm
RTI, Strength
0.75mm
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
°C
°C
°C
|
50
110
110
50
85
90
50
90
95
|
Other
Density
Mold Shrinkage
Flow, 60x60x2mm
Transverse, 60x60x2mm
|
ISO 1183
|
3 3
kg/m (g/cm )
%
|
1420 (1.42)
1.8
2.1
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
Hold Pressure Range
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
MPa (kpsi)
|
210-220 (410-430)
215 (420)
80-100 (175-212)
90 (195)
2-4
80 (175)
<0.2
90-110 (13-15)
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science and Delrin® are trademarks or registered trademarks of DuPont Company. Copyright© 2006.