- 产 品：PEEK LX04420C 含有碳纤维,是一个导电聚醚醚酮树脂
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP* STAT-KON* COMPOUND
LNP STAT-KON RESIN ALL SERIES
LNP* Stat-Kon* composites contain electrically conductive additives. They and span a broad range of surface resistivity and electrical activity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding. Stat-Kon* composites offer cost-effective solutions when products must avoid static electricity buildup or discharge. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™ STAT-KON™ Compound PEEK LX04420C 塑料物性表
Also known as:LNP™ Stat-kon™ Compound PDX-L-04420 CCS Product reorder name:LX04420C
LNP* Stat-kon* LX04420C is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yield | 1520 | kgf/cm² | ASTM D 638 |
| Tensile Stress,break | 1520 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yield | 2.3 | % | ASTM D 638 |
| Tensile Strain,break | 2.3 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 122300 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 2460 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 110000 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield | 149 | MPa | ISO 527 |
| Tensile Stress,break | 149 | MPa | ISO 527 |
| Tensile Strain,yield | 2.1 | % | ISO 527 |
| Tensile Strain,break | 2.1 | % | ISO 527 |
| Tensile Modulus,1mm/min | 11500 | MPa | ISO 527 |
| Flexural Stress | 241 | MPa | ISO 178 |
| Flexural Modulus | 10270 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 58 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 4 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Energy @ peak,23℃ | 24 | cm-kgf | ASTM D 3763 |
| Multiaxial Impact | 24 | cm-kgf | ISO 6603 |
| Izod Impact,unnotched 80*10*4 +23℃ | 212 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 13 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,3.2mm,unannealed | 300 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 3.96E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 1.62E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 4.12E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 1.63E-05 | 1/℃ | ISO 11359-2 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 246 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.36 | g/cm³ | ASTM D 792 |
| Mold Shrinkage,flow,24 hrs(5) | 0.3 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.6 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 0.34 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.62 | % | ISO 294 |
| Density | 1.36 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+06-1.E+08 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+06-1.E+08 | Ohm | ASTM D 257 |
| Source GMD,last updated:2006/03/28 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 120-150 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.1 | % |
| Melt Temperature | 380-390 | ℃ |
| Front-Zone 3 Temperature | 380-395 | ℃ |
| Middle-Zone 2 Temperature | 365-375 | ℃ |
| Rear-Zone 1 Temperature | 350-360 | ℃ |
| Mold Temperature | 140-165 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 60-100 | rpm |
| Source GMD,last updated:2006/03/28 | ||