- 产 品：PC/ABS XCY620S 高耐热,抗水解和热老化
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Cycoloy* Visualfx* Resin
Tough Yet Beautiful
Cycoloy PC/ABS Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding while still offering the impact and processing advantage that Cycoloy Resin is known for. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Sparkle and Porcelain effects as well as several metallic and natural material effects. Available in a variety of colors and base resins.
Cycoloy* Resin XCY620S 数据
PC+ ABS Automotive applications, Good flow/impact/high heat resistance balance, good properties retention after Hydrolytic and Heat Aging
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Flexural Stress,yld,1.3mm/min,50mm span | 870 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 23400 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,50mm/min | 54 | MPa | ISO 527 |
| Tensile Stress,break,50mm/min | 56 | MPa | ISO 527 |
| Tensile Strain,yield,50mm/min | 4.5 | % | ISO 527 |
| Tensile Strain,break,50mm/min | 100 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2200 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 82 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 2200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Instrumented Impact Total Energy,23℃ | 560 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Total Energy,-30℃ | 662 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*3 +23℃ | PASSES | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 55 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 40 | kJ/m² | ISO 180/1A |
| Charpy 23℃,Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
| Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 129 | ℃ | ASTM D 1525 |
| HDT,0.45 MPa,3.2mm,unannealed | 128 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 108 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 7.00E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 7.00E-05 | 1/℃ | ASTM E 831 |
| Ball Pressure Test,75℃ +/- 2℃ | PASSES | - | IEC 60695-10-2 |
| Ball Pressure Test,approximate maximum | 100 | ℃ | IEC 60695-10-2 |
| Vicat Softening Temp,Rate B/120 | 130 | ℃ | ISO 306 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 126 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 106 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.14 | - | ASTM D 792 |
| Mold Shrinkage,flow,3.2mm(5) | 0.5-0.7 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2mm(5) | 0.5-0.7 | % | SABIC Method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Water Absorption,23℃/24hrs | 0.3 | % | ISO 62-1 |
| Water Absorption,(23℃/sat) | 0.4 | % | ISO 62 |
| Moisture Absorption(23℃/50% RH) | 0.13 | % | ISO 62 |
| Melt Volume Rate,MVR at 260℃/5.0 kg | 20 | cm³/10 min | ISO 1133 |
| Melt Volume Rate,MVR at 265℃/5.0 kg | 25 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+16 | Ohm-cm | IEC 60093 |
| Surface Resistivity,ROA | >1.E+16 | Ohm | IEC 60093 |
| Dielectric Strength,in oil,0.8mm | 39 | kV/mm | IEC 60243-1 |
| Dielectric Strength,in oil,1.6mm | 25 | kV/mm | IEC 60243-1 |
| Dielectric Strength,in oil,3.2mm | 17 | kV/mm | IEC 60243-1 |
| Source GMD,last updated:2012/05/02 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 95-105 | ℃ |
| Drying Time | 2-4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260-290 | ℃ |
| Nozzle Temperature | 240-280 | ℃ |
| Front-Zone 3 Temperature | 250-290 | ℃ |
| Middle-Zone 2 Temperature | 250-290 | ℃ |
| Rear-Zone 1 Temperature | 230-260 | ℃ |
| Hopper Temperature | 60-80 | ℃ |
| Mold Temperature | 60-90 | ℃ |
| Source GMD,last updated:2012/05/02 | ||
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.