Cycoloy* Visualfx* Resin
Tough Yet Beautiful
Cycoloy PC/ABS Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding while still offering the impact and processing advantage that Cycoloy Resin is known for. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Sparkle and Porcelain effects as well as several metallic and natural material effects. Available in a variety of colors and base resins.

Cycoloy* Resin XCM840 数据
High stiffness PC/ABS blend offering practical impact, low CTE, high heat resistance, with good aesthetics suitable for injection molding

Property
TYPICAL PROPERTIES (1)

MECHANICAL	Value	Unit	Standard
Tensile Stress,yld,Type I,5mm/min	570	kgf/cm²	ASTM D 638
Tensile Stress,brk,Type I,5mm/min	470	kgf/cm²	ASTM D 638
Tensile Strain,yld,Type I,5mm/min	4	%	ASTM D 638
Tensile Modulus,5mm/min	43800	kgf/cm²	ASTM D 638
Tensile Stress,yield,5mm/min	56	MPa	ISO 527
Tensile Stress,break,5mm/min	47	MPa	ISO 527
Tensile Strain,yield,5mm/min	4	%	ISO 527
Tensile Strain,break,5mm/min	50	%	ISO 527
Tensile Modulus,1mm/min	4300	MPa	ISO 527
Flexural Stress,yield,2mm/min	100	MPa	ISO 178
Flexural Modulus,2mm/min	4000	MPa	ISO 178
IMPACT	Value	Unit	Standard
Instrumented Impact Total Energy,23℃	611	cm-kgf	ASTM D 3763
Izod Impact,notched 80*10*3 +23℃	15	kJ/m²	ISO 180/1A
Izod Impact,notched 80*10*3 -30℃	8	kJ/m²	ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm	37	kJ/m²	ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm	10	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
HDT,1.82 MPa,3.2mm,unannealed	120	℃	ASTM D 648
CTE,-40℃ to 40℃,flow	4.60E-05	1/℃	ASTM E 831
CTE,-40℃ to 40℃,xflow	6.10E-05	1/℃	ASTM E 831
CTE,-40℃ to 40℃,flow	4.60E-05	1/℃	ISO 11359-2
CTE,-40℃ to 40℃,xflow	6.10E-05	1/℃	ISO 11359-2
Vicat Softening Temp,Rate B/50	138	℃	ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm	120	℃	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.27	-	ASTM D 792
Mold Shrinkage,flow,3.2mm(5)	0.5-0.7	%	SABIC Method
Mold Shrinkage,xflow,3.2mm(5)	0.5-0.7	%	SABIC Method
Density	1.27	g/cm³	ISO 1183
Melt Volume Rate,MVR at 260℃/5.0 kg	10	cm³/10 min	ISO 1133
Melt Volume Rate,MVR at 265℃/5.0 kg	12	cm³/10 min	ISO 1133
Source GMD,last updated:2012/04/12

Parameter Injection Molding	Value	Unit
Drying Temperature	120-125	℃
Drying Time	4-6	hrs
Maximum Moisture Content	0.01	%
Melt Temperature	270-300	℃
Nozzle Temperature	260-290	℃
Front-Zone 3 Temperature	270-300	℃
Middle-Zone 2 Temperature	265-290	℃
Rear-Zone 1 Temperature	260-270	℃
Mold Temperature	60-100	℃
Back Pressure	0.3-0.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	30-80	%
Vent Depth	0.038-0.076	mm
Source GMD,last updated:2012/04/12

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.