Cycoloy* Visualfx* Resin
Tough Yet Beautiful
Cycoloy PC/ABS Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding while still offering the impact and processing advantage that Cycoloy Resin is known for. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Sparkle and Porcelain effects as well as several metallic and natural material effects. Available in a variety of colors and base resins.

Cycoloy* Resin CY6310 数据
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow / impact balance for a wide variety of thin wall or large size applications including business equipment, enclosures, among others.

Property
TYPICAL PROPERTIES (1)

MECHANICAL	Value	Unit	Standard
Tensile Stress,yld,Type I,50mm/min	640	kgf/cm²	ASTM D 638
Tensile Stress,brk,Type I,50mm/min	500	kgf/cm²	ASTM D 638
Tensile Strain,yld,Type I,50mm/min	4.2	%	ASTM D 638
Tensile Strain,brk,Type I,50mm/min	>50	%	ASTM D 638
Tensile Modulus,5mm/min	27500	kgf/cm²	ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span	1020	kgf/cm²	ASTM D 790
Flexural Modulus,1.3mm/min,50mm span	27500	kgf/cm²	ASTM D 790
Tensile Stress,yield,50mm/min	63	MPa	ISO 527
Tensile Stress,break,50mm/min	51	MPa	ISO 527
Tensile Strain,yield,50mm/min	4.4	%	ISO 527
Tensile Strain,break,50mm/min	>50	%	ISO 527
Tensile Modulus,1mm/min	2700	MPa	ISO 527
Flexural Stress,yield,2mm/min	91	MPa	ISO 178
Flexural Modulus,2mm/min	2650	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact,notched,23℃	61	cm-kgf/cm	ASTM D 256
Izod Impact,notched,-30℃	11	cm-kgf/cm	ASTM D 256
Multiaxial Impact	1070	cm-kgf	ISO 6603
Instrumented Impact Total Energy,23℃	662	cm-kgf	ASTM D 3763
Izod Impact,unnotched 80*10*3 +23℃	NB	kJ/m²	ISO 180/1U
Izod Impact,notched 80*10*3 +23℃	50	kJ/m²	ISO 180/1A
Izod Impact,notched 80*10*3 -30℃	13	kJ/m²	ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm	55	kJ/m²	ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm	14	kJ/m²	ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*3 sp=62mm	NB	kJ/m²	ISO 179/1eU
THERMAL	Value	Unit	Standard
Vicat Softening Temp,Rate B/50	109	℃	ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed	100	℃	ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed	88	℃	ASTM D 648
CTE,-40℃ to 40℃,flow	6.80E-05	1/℃	ASTM E 831
CTE,-40℃ to 40℃,xflow	7.00E-05	1/℃	ASTM E 831
CTE,-40℃ to 40℃,flow	6.80E-05	1/℃	ISO 11359-2
CTE,-40℃ to 40℃,xflow	7.00E-05	1/℃	ISO 11359-2
Ball Pressure Test,75℃ +/- 2℃	Pass	-	IEC 60695-10-2
Ball Pressure Test,approximate maximum	95	℃	IEC 60695-10-2
Vicat Softening Temp,Rate B/50	109	℃	ISO 306
Vicat Softening Temp,Rate B/120	111	℃	ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm	90	℃	ISO 75/Af
Relative Temp Index,Elec	85	℃	UL 746B
Relative Temp Index,Mech w/impact	85	℃	UL 746B
Relative Temp Index,Mech w/o impact	85	℃	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.16	-	ASTM D 792
Mold Shrinkage,flow,3.2mm(5)	0.4-0.6	%	SABIC Method
Melt Flow Rate,250℃/2.16 kgf	16	g/10 min	ASTM D 1238
Melt Flow Rate,260℃/2.16 kgf	20	g/10 min	ASTM D 1238
Density	1.16	g/cm³	ISO 1183
Water Absorption,(23℃/sat)	0.6	%	ISO 62
Moisture Absorption(23℃/50% RH)	0.2	%	ISO 62
Melt Volume Rate,MVR at 260℃/2.16 kg	19	cm³/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Hot Wire Ignition{PLC)	3	PLC Code	UL 746A
High Ampere Arc Ign,surface{PLC}	0	PLC Code	UL 746A
Volume Resistivity	>1.E+15	Ohm-cm	IEC 60093
Surface Resistivity,ROA	>1.E+15	Ohm	IEC 60093
Comparative Tracking Index	575	V	IEC 60112
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant,94V-2 Flame Class Rating(3)(4)	0.75	mm	UL 94 by SABIC-IP
UL Compliant,94V-0 Flame Class Rating(3)(4)	1.5	mm	UL 94 by SABIC-IP
UL Compliant,94-5VA Rating(3)(4)	2.9	mm	UL 94 by SABIC-IP
UL Compliant,94-5VB Rating(3)(4)	2.3	mm	UL 94 by SABIC-IP
UL Recognized,94V-2 Flame Class Rating(3)	0.75	mm	UL 94
UL Recognized,94V-0 Flame Class Rating(3)	1.5	mm	UL 94
UL Recognized,94-5VA Rating(3)	2.9	mm	UL 94
UL Recognized,94-5VB Rating(3)	2.3	mm	UL 94
Glow Wire Flammability Index 960℃,passes at	3	mm	IEC 60695-2-12
Oxygen Index(LOI)	30	%	ISO 4589
Source GMD,last updated:2007/08/16

Parameter Injection Molding	Value	Unit
Drying Temperature	90-100	℃
Drying Time	2-4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250-280	℃
Nozzle Temperature	230-270	℃
Front-Zone 3 Temperature	240-280	℃
Middle-Zone 2 Temperature	230-270	℃
Rear-Zone 1 Temperature	210-240	℃
Hopper Temperature	60-80	℃
Mold Temperature	60-90	℃
Source GMD, last updated:2007/08/16

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
PC/ABS合金塑料报价网：http://www.pa66-suliao.com/product/gcsuliao/PC/ABS/