PC/ABS CX7510 不含氯和溴的阻燃剂,高抗冲击
  • 产 品:PC/ABS CX7510 不含氯和溴的阻燃剂,高抗冲击
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Cycoloy* Visualfx* Resin
Tough Yet Beautiful
Cycoloy PC/ABS Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding while still offering the impact and processing advantage that Cycoloy Resin is known for. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Sparkle and Porcelain effects as well as several metallic and natural material effects. Available in a variety of colors and base resins.

Cycoloy* Resin CX7510 数据
Cycoloy* CX7510 resin is an injection moldable, flame retardant PC/ABS blend, with non-chlorinated & non-brominated flame retardants. Key features of Cycoloy CX7510 resin include high heat, high flow and good impact resistance.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 660 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 490 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 4 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 36 % ASTM D 638
Tensile Modulus,50mm/min 26300 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 980 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 23700 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 64 MPa ISO 527
Tensile Stress,break,50mm/min 48 MPa ISO 527
Tensile Strain,yield,50mm/min 4.5 % ISO 527
Tensile Strain,break,50mm/min 36 % ISO 527
Tensile Modulus,1mm/min 2540 MPa ISO 527
Flexural Stress,yield,2mm/min 99 MPa ISO 178
Flexural Modulus,2mm/min 2620 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 65 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 13 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 662 cm-kgf ASTM D 3763
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 36 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 113 ASTM D 1525
HDT,1.82 MPa,6.4mm,unannealed 106 ASTM D 648
CTE,-40℃ to 40℃,flow 6.90E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.20E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 7.20E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 7.50E-05 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 115 ISO 306
Vicat Softening Temp,Rate B/120 118 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 95 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.18 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.56-0.63 % SABIC Method
Melt Flow Rate,260℃/2.16 kgf 16 g/10 min ASTM D 1238
Melt Flow Rate,260℃/5.0 kgf 45 g/10 min ASTM D 1238
Density 1.18 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.11 % ISO 62
Moisture Absorption(23℃/50% RH) 0.05 % ISO 62
Melt Volume Rate,MVR at 260℃/5.0 kg 41 cm³/10 min ISO 1133
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-0 Flame Class Rating(3) 1.5 mm UL 94
UL Recognized,94-5VB Rating(3) 1.5 mm UL 94
Source GMD,last updated:2008/04/09
Parameter Injection Molding Value Unit
Drying Temperature 90-100
Drying Time 2-4 hrs
Drying Time(Cumulative) 8 hrs
Maximum Moisture Content 0.04 %
Melt Temperature 270-300
Nozzle Temperature 265-300
Front-Zone 3 Temperature 265-300
Middle-Zone 2 Temperature 260-300
Rear-Zone 1 Temperature 260-300
Mold Temperature 60-90
Back Pressure 0.3-0.7 MPa
Screw Speed 40-70 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.038-0.076 mm
Source GMD,last updated:2008/04/09
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.