Cycoloy* Visualfx* Resin
Tough Yet Beautiful
Cycoloy PC/ABS Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding while still offering the impact and processing advantage that Cycoloy Resin is known for. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Sparkle and Porcelain effects as well as several metallic and natural material effects. Available in a variety of colors and base resins.

Cycoloy* Resin FXC630ME 数据
Color package may affect performance. PC+ABS, ECO-conforming flame retardant with metallic or pearlescent appearance.

Property
TYPICAL PROPERTIES (1)

MECHANICAL	Value	Unit	Standard
Tensile Stress,yld,Type I,50mm/min	600	kgf/cm²	ASTM D 638
Tensile Stress,brk,Type I,50mm/min	470	kgf/cm²	ASTM D 638
Tensile Strain,yld,Type I,50mm/min	4	%	ASTM D 638
Tensile Strain,brk,Type I,50mm/min	20	%	ASTM D 638
Tensile Modulus,50mm/min	31600	kgf/cm²	ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span	960	kgf/cm²	ASTM D 790
Flexural Modulus,1.3mm/min,50mm span	27400	kgf/cm²	ASTM D 790
Tensile Stress,yield,50mm/min	55	MPa	ISO 527
Tensile Stress,break,50mm/min	45	MPa	ISO 527
Tensile Strain,yield,50mm/min	5	%	ISO 527
Tensile Strain,break,50mm/min	15	%	ISO 527
Tensile Modulus,1mm/min	2400	MPa	ISO 527
Flexural Stress,yield,2mm/min	82	MPa	ISO 178
Flexural Modulus,2mm/min	2400	MPa	ISO 178
Hardness,H358/30	99	MPa	ISO 2039-1
Hardness,Rockwell R	121	-	ISO 2039-2
IMPACT	Value	Unit	Standard
Izod Impact,notched,23℃	16	cm-kgf/cm	ASTM D 256
Instrumented Impact Total Energy,23℃	483	cm-kgf	ASTM D 3763
Izod Impact,notched 80*10*4 +23℃	24	kJ/m²	ISO 180/1A
Izod Impact,notched 80*10*4 -30℃	12	kJ/m²	ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm	25	kJ/m²	ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm	13	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp,Rate B/50	98	℃	ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed	90	℃	ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed	82	℃	ASTM D 648
CTE,-40℃ to 40℃,flow	7.20E-05	1/℃	ASTM E 831
CTE,-40℃ to 40℃,xflow	7.20E-05	1/℃	ASTM E 831
Thermal Conductivity	0.2	W/m-℃	ISO 8302
CTE,23℃ to 60℃,flow	8.00E-05	1/℃	ISO 11359-2
CTE,23℃ to 60℃,xflow	8.00E-05	1/℃	ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃	PASSES	-	IEC 60695-10-2
Vicat Softening Temp,Rate B/50	128	℃	ISO 306
Vicat Softening Temp,Rate B/120	130	℃	ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm	128	℃	ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm	108	℃	ISO 75/Ae
Relative Temp Index,Elec	60	℃	UL 746B
Relative Temp Index,Mech w/impact	60	℃	UL 746B
Relative Temp Index,Mech w/o impact	60	℃	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.19	-	ASTM D 792
Mold Shrinkage,flow,3.2mm(5)	0.3-0.5	%	SABIC Method
Melt Flow Rate,260℃/2.16 kgf	14	g/10 min	ASTM D 1238
Density	1.18	g/cm³	ISO 1183
Density(Molded)	1.2	g/cm³	ISO 1183
Melt Volume Rate,MVR at 260℃/2.16 kg	14	cm³/10 min	ISO 1133
Melt Volume Rate,MVR at 260℃/5.0 kg	22	cm³/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	>1.E+15	Ohm-cm	IEC 60093
Surface Resistivity,ROA	>1.E+15	Ohm	IEC 60093
Dielectric Strength,in oil,0.8mm	35	kV/mm	IEC 60243-1
Dielectric Strength,in oil,1.6mm	25	kV/mm	IEC 60243-1
Dielectric Strength,in oil,3.2mm	17	kV/mm	IEC 60243-1
Relative Permittivity,1 MHz	2.7	-	IEC 60250
Dissipation Factor,50/60 Hz	0.003	-	IEC 60250
Dissipation Factor,1 MHz	0.005	-	IEC 60250
Relative Permittivity,50/60 Hz	2.8	-	IEC 60250
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized,94V-2 Flame Class Rating(3)	1.01	mm	UL 94
UL Recognized,94V-1 Flame Class Rating(3)	1.19	mm	UL 94
UL Recognized,94V-0 Flame Class Rating(3)	1.49	mm	UL 94
UL Recognized,94-5VB Rating(3)	2	mm	UL 94
Oxygen Index(LOI)	23	%	ISO 4589
Source GMD,last updated:2001/04/11

Parameter Injection Molding	Value	Unit
Drying Temperature	80-90	℃
Drying Time	3-4	hrs
Drying Time(Cumulative)	8	hrs
Maximum Moisture Content	0.04	%
Melt Temperature	245-275	℃
Nozzle Temperature	245-275	℃
Front-Zone 3 Temperature	245-275	℃
Middle-Zone 2 Temperature	220-265	℃
Rear-Zone 1 Temperature	220-255	℃
Mold Temperature	60-80	℃
Back Pressure	0.3-0.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	30-80	%
Vent Depth	0.038-0.076	mm
Source GMD,last updated:2001/04/11

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.