Cycoloy* High Modulus Non-FR Resin
Non-Flame Retardant Dimensionally Stable Resins
Our portfolio of low CTE resins is a series of amorphous filled PC/ABS blends which offer outstanding dimensional stability and high modulus with superior ductility. Individual grades are suitable for processing by injection molding and monolayer or multi-layer sheet extrusion. These products can also provide a high quality surface suitable for painting.

Cycoloy* Resin CP8930 数据
High heat, PC/ABS for automotive electro plating applications, excellent balance in flow/impact

Property
TYPICAL PROPERTIES (1)

MECHANICAL	Value	Unit	Standard
Tensile Stress,yld,Type I,50mm/min	530	kgf/cm²	ASTM D 638
Tensile Stress,brk,Type I,50mm/min	470	kgf/cm²	ASTM D 638
Tensile Strain,yld,Type I,50mm/min	4.2	%	ASTM D 638
Tensile Strain,brk,Type I,50mm/min	110	%	ASTM D 638
Tensile Modulus,5mm/min	24100	kgf/cm²	ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span	830	kgf/cm²	ASTM D 790
Flexural Modulus,1.3mm/min,50mm span	24100	kgf/cm²	ASTM D 790
Tensile Stress,yield,50mm/min	51	MPa	ISO 527
Tensile Stress,break,50mm/min	47	MPa	ISO 527
Tensile Strain,yield,50mm/min	4	%	ISO 527
Tensile Strain,break,50mm/min	100	%	ISO 527
Tensile Modulus,1mm/min	2400	MPa	ISO 527
Flexural Stress,yield,2mm/min	65	MPa	ISO 178
Flexural Modulus,2mm/min	2200	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact,notched,23℃	57	cm-kgf/cm	ASTM D 256
Izod Impact,notched,-30℃	38	cm-kgf/cm	ASTM D 256
Instrumented Impact Total Energy,23℃	560	cm-kgf	ASTM D 3763
Izod Impact,notched 80*10*3 +23℃	50	kJ/m²	ISO 180/1A
Izod Impact,notched 80*10*3 -30℃	35	kJ/m²	ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm	50	kJ/m²	ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm	35	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp,Rate B/50	126	℃	ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed	103	℃	ASTM D 648
CTE,-40℃ to 40℃,flow	7.20E-05	1/℃	ASTM E 831
CTE,-40℃ to 40℃,xflow	7.80E-05	1/℃	ASTM E 831
CTE,-40℃ to 40℃,flow	7.20E-05	1/℃	ISO 11359-2
CTE,-40℃ to 40℃,xflow	7.80E-05	1/℃	ISO 11359-2
Ball Pressure Test,75℃ +/- 2℃	PASSES	-	IEC 60695-10-2
Vicat Softening Temp,Rate B/50	126	℃	ISO 306
Vicat Softening Temp,Rate B/120	129	℃	ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm	103	℃	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.13	-	ASTM D 792
Mold Shrinkage,flow,3.2mm(5)	0.5-0.8	%	SABIC Method
Mold Shrinkage,xflow,3.2mm(5)	0.5-0.7	%	SABIC Method
Melt Flow Rate,260℃/5.0 kgf	16	g/10 min	ASTM D 1238
Density	1.1	g/cm³	ISO 1183
Water Absorption,(23℃/sat)	0.4	%	ISO 62
Moisture Absorption(23℃/50% RH)	0.2	%	ISO 62
Melt Volume Rate,MVR at 265℃/5.0 kg	20	cm³/10 min	ISO 1133
Source GMD,last updated:2004/12/21

Parameter Injection Molding	Value	Unit
Drying Temperature	100-105	℃
Drying Time	3-4	hrs
Drying Time(Cumulative)	8	hrs
Maximum Moisture Content	0.04	%
Melt Temperature	260-290	℃
Nozzle Temperature	260-290	℃
Front-Zone 3 Temperature	255-290	℃
Middle-Zone 2 Temperature	255-290	℃
Rear-Zone 1 Temperature	250-280	℃
Mold Temperature	75-100	℃
Back Pressure	0.3-0.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	30-80	%
Vent Depth	0.038-0.076	mm
Source GMD,last updated:2004/12/21

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.