Cycoloy* High Modulus FR Resin
High Modulus, Dimensionally Stable Resins
The HMD Resin portfolio is a series of filled amorphous PC/ABS blends offering outstanding dimensional stability and high modulus while maintaining good ductility and low CTE. HMD resins provide high surface quality that can be painted or provide the structural layer in a multi-layer sheet extrusion.

Cycoloy* Resin CM6140 数据
Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffness, balanced properties in flow, impact and heat designed for various thin wall applications.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 660 kgf/cm² ASTM D 638
Tensile Stress,yld,Type I,5mm/min 660 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 500 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 4 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 100 % ASTM D 638
Tensile Modulus,5mm/min 35600 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 1010 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 33600 kgf/cm² ASTM D 790
Tensile Stress,break,5mm/min 50 MPa ISO 527
Tensile Strain,yield,5mm/min 3.5 % ISO 527
Tensile Strain,break,50mm/min 15 % ISO 527
Tensile Modulus,1mm/min 3200 MPa ISO 527
Flexural Stress,yield,2mm/min 97 MPa ISO 178
Flexural Modulus,2mm/min 3450 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 20 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 8 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 509 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*3 +23℃ 10 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 5 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm 10 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm 5 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 91 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 83 ASTM D 648
HDT,0.45 MPa,6.4mm,unannealed 97 ASTM D 648
HDT,1.82 MPa,6.4mm,unannealed 89 ASTM D 648
CTE,-40℃ to 40℃,flow 5.50E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 6.00E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 5.50E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 6.00E-05 1/℃ ISO 11359-2
Ball Pressure Test,75℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate B/50 98 ISO 306
Vicat Softening Temp,Rate B/120 102 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 80 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.26 - ASTM D 792
Water Absorption,24 hours 0.1 % ASTM D 570
Moisture Absorption,50% RH,24 hrs 0.01 % ASTM D 570
Mold Shrinkage,flow,3.2mm(5) 0.3-0.5 % SABIC Method
Mold Shrinkage,xflow,3.2mm(5) 0.4-0.6 % SABIC Method
Melt Flow Rate,260℃/2.16 kgf 17.5 g/10 min ASTM D 1238
Density 1.25 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.09 % ISO 62
Moisture Absorption(23℃/50% RH) 0.01 % ISO 62
Melt Volume Rate,MVR at 220℃/5.0 kg 14 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Volume Resistivity 2.68E+16 Ohm-cm ASTM D 257
Surface Resistivity 3.54E+15 Ohm ASTM D 257
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-1 Flame Class Rating(3) 0.6 mm UL 94
UL Recognized,94V-0 Flame Class Rating(3) 0.8 mm UL 94
UL Recognized,94-5VB Rating(3) 1.5 mm UL 94
Glow Wire Flammability Index 960℃,passes at 0.8 mm IEC 60695-2-12
Glow Wire Ignitability Temperature,1.0mm 850 IEC 60695-2-13
Glow Wire Ignitability Temperature,3.0mm 800 IEC 60695-2-13
Source GMD,last updated:2004/12/02
Parameter Injection Molding Value Unit
Drying Temperature 90
Drying Time >4 hrs
Maximum Moisture Content 0.04 %
Melt Temperature 275-300
Nozzle Temperature 280-300
Front-Zone 3 Temperature 280-300
Middle-Zone 2 Temperature 275-300
Rear-Zone 1 Temperature 275-300
Mold Temperature 60-80
Source GMD,last updated:2004/12/02
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.