PC/ABS CU1650 紫外线稳定,良好的流动和抗冲击
  • 产 品:PC/ABS CU1650 紫外线稳定,良好的流动和抗冲击
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Cycoloy* General Purpose Non-FR Resin
Specially Formulated to Meet Your Needs
This portfolio of Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) alloys is designed for specialized engineering or formulation to meet specific customer requirements. Please feel free to contact us to discuss your needs.

Cycoloy* Resin CU1650 数据
UV stabilized, non-FR PC/ABS of excellent flow and impact performance

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 550 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 540 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 4.5 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 120 % ASTM D 638
Tensile Modulus,5mm/min 23400 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 900 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 23400 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 54 MPa ISO 527
Tensile Stress,break,50mm/min 53 MPa ISO 527
Tensile Strain,yield,50mm/min 4.5 % ISO 527
Tensile Strain,break,50mm/min 120 % ISO 527
Tensile Modulus,1mm/min 2250 MPa ISO 527
Flexural Stress,yield,2mm/min 80 MPa ISO 178
Flexural Modulus,2mm/min 2200 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 60 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 40 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 560 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*3 +23℃ 65 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 30 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm 65 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm 30 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 126 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 107 ASTM D 648
CTE,-40℃ to 40℃,flow 7.00E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.00E-05 1/℃ ASTM E 831
Thermal Conductivity 0.2 W/m-℃ ISO 8302
CTE,-40℃ to 40℃,flow 8.00E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 8.00E-05 1/℃ ISO 11359-2
Ball Pressure Test,75℃ +/- 2℃ Pass - IEC 60695-10-2
Vicat Softening Temp,Rate B/50 126 ISO 306
Vicat Softening Temp,Rate B/120 127 ISO 306
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 126 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 105 ISO 75/Af
Relative Temp Index,Elec 60 UL 746B
Relative Temp Index,Mech w/impact 60 UL 746B
Relative Temp Index,Mech w/o impact 60 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.14 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.5-0.7 % SABIC Method
Mold Shrinkage,xflow,3.2mm(5) 0.5-0.7 % SABIC Method
Melt Flow Rate,260℃/5.0 kgf 28 g/10 min ASTM D 1238
Density 1.14 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.4 % ISO 62
Moisture Absorption(23℃/50% RH) 0.15 % ISO 62
Melt Volume Rate,MVR at 260℃/2.16 kg 8 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 260℃/5.0 kg 25 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity,ROA >1.E+15 Ohm IEC 60093
Dielectric Strength,in oil,0.8mm 35 kV/mm IEC 60243-1
Dielectric Strength,in oil,1.6mm 25 kV/mm IEC 60243-1
Dielectric Strength,in oil,3.2mm 17 kV/mm IEC 60243-1
FLAME CHARACTERISTICS Value Unit Standard
Glow Wire Ignitability Temperature,3.0mm 750 IEC 60695-2-13
Source GMD,last updated:2005/03/01
Parameter Injection Molding Value Unit
Drying Temperature 95-105
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 260-290
Nozzle Temperature 240-280
Front-Zone 3 Temperature 250-290
Middle-Zone 2 Temperature 250-290
Rear-Zone 1 Temperature 230-260
Hopper Temperature 60-80
Mold Temperature 60-90
Source GMD,last updated:2005/03/01
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.