PC/ABS CE8510 挤出级,低粘度
  • 产 品:PC/ABS CE8510 挤出级,低粘度
  • 产 地: 沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Cycoloy* Extrusion Resin
Impact & Ductility for Large Panels
A Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) alloy designed for sheet and other extrusions. Can be used for such applications as body and other large panels, as well as corrugated electrical conduit. Provides high impact strength and ductility, Class A paintable surfaces, and dimensional and heat aging stability.

Cycoloy* Resin CE8510 数据
Extrusion grade PC/ABS. Low viscosity, high impact and ductility.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 580 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 570 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 4.9 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 125 % ASTM D 638
Tensile Modulus,5mm/min 22100 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 860 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 23900 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 50 MPa ISO 527
Tensile Stress,break,50mm/min 45 MPa ISO 527
Tensile Strain,yield,50mm/min 4 % ISO 527
Tensile Strain,break,50mm/min >50 % ISO 527
Tensile Modulus,1mm/min 2250 MPa ISO 527
Flexural Stress,yield,2mm/min 85 MPa ISO 178
Flexural Modulus,2mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 66 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 54 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 611 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*3 +23℃ 50 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 35 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm 50 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm 35 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 118 ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed 124 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 107 ASTM D 648
CTE,-40℃ to 40℃,flow 7.20E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 8.00E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 7.20E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 8.00E-05 1/℃ ISO 11359-2
Ball Pressure Test,75℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate B/50 118 ISO 306
Vicat Softening Temp,Rate B/120 122 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 120 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.14 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.5-0.7 % SABIC Method
Mold Shrinkage,xflow,3.2mm(5) 0.5-0.7 % SABIC Method
Melt Flow Rate,260℃/5.0 kgf 8.5 g/10 min ASTM D 1238
Density 1.14 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.1 % ISO 62
Moisture Absorption(23℃/50% RH) 0.1 % ISO 62
Melt Volume Rate,MVR at 265℃/5.0 kg 10 cm³/10 min ISO 1133
Source GMD,last updated:2004/09/03
Parameter Film Extrusion Value Unit
Drying Temperature 90-110
Drying Time 4 hrs
Drying Time(Cumulative) 6-8 hrs
Maximum Moisture Content 0.04 %
Barrell Temperature-Rear 220-250
Barrell Temperature-Middle 220-250
Barrell Temperature-Front 220-250
Die Temperature 220-250
Roll Temperature 200-250
Source GMD,last updated:2004/09/03
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.