PC/ABS CY9640 高冲击,高流动,耐热老化
  • 产 品:PC/ABS CY9640 高冲击,高流动,耐热老化
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Cycoloy* Resin CY9640 英文数据
PC+ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 560 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 530 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 4.7 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 115 % ASTM D 638
Tensile Modulus,5mm/min 23400 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 900 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 23400 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 54 MPa ISO 527
Tensile Stress,break,50mm/min 51 MPa ISO 527
Tensile Strain,yield,50mm/min 4.5 % ISO 527
Tensile Strain,break,50mm/min 115 % ISO 527
Tensile Modulus,1mm/min 2200 MPa ISO 527
Flexural Stress,yield,2mm/min 83 MPa ISO 178
Flexural Modulus,2mm/min 2200 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 65 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 48 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 571 cm-kgf ASTM D 3763
Instrumented Impact Total Energy,-30℃ 713 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*3 +23℃ 70 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 45 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm 70 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm 45 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 127 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 107 ASTM D 648
CTE,-40℃ to 40℃,flow 7.00E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.00E-05 1/℃ ASTM E 831
Thermal Conductivity 0.2 W/m-℃ ISO 8302
CTE,-40℃ to 40℃,flow 8.00E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 8.00E-05 1/℃ ISO 11359-2
Ball Pressure Test,75℃ +/- 2℃ Pass - IEC 60695-10-2
Vicat Softening Temp,Rate B/50 127 ISO 306
Vicat Softening Temp,Rate B/120 129 ISO 306
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 126 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 105 ISO 75/Af
Relative Temp Index,Elec 60 UL 746B
Relative Temp Index,Mech w/impact 60 UL 746B
Relative Temp Index,Mech w/o impact 60 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.14 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.5-0.7 % SABIC Method
Mold Shrinkage,xflow,3.2mm(5) 0.5-0.7 % SABIC Method
Melt Flow Rate,260℃/5.0 kgf 22 g/10 min ASTM D 1238
Density 1.14 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.4 % ISO 62
Moisture Absorption(23℃/50% RH) 0.15 % ISO 62
Melt Volume Rate,MVR at 260℃/5.0 kg 21 cm³/10 min ISO 1133
Melt Viscosity,260℃,1500 sec-1 195 Pa-s ISO 11443
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity,ROA >1.E+15 Ohm IEC 60093
Dielectric Strength,in oil,0.8mm 35 kV/mm IEC 60243-1
Dielectric Strength,in oil,1.6mm 25 kV/mm IEC 60243-1
Dielectric Strength,in oil,3.2mm 17 kV/mm IEC 60243-1
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94HB Flame Class Rating(3) 1.5 mm UL 94
UL Recognized,94HB Flame Class Rating 2nd value(3) 3 mm UL 94
Glow Wire Ignitability Temperature,3.0mm 750 IEC 60695-2-13
Source GMD,last updated:2004/11/19
Processing Parameter
Injection Molding Value Unit
Drying Temperature 95-105
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 260-290
Nozzle Temperature 240-280
Front-Zone 3 Temperature 250-290
Middle-Zone 2 Temperature 250-290
Rear-Zone 1 Temperature 230-260
Hopper Temperature 60-80
Mold Temperature 60-90
Source GMD,last updated:2004/11/19
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.

PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

Disclaimer : THE MATERIALS, PRODUCTS AND SERVICES OF SABIC INNOVATIVE PLASTICS HOLDING BV, ITS SUBSIDIARIES AND AFFILIATES ("SELLER"), ARE SOLD SUBJECT TO SELLER'S STANDARD CONDITIONS OF SALE, WHICH CAN BE FOUND AT http://www.pa66-suliao.com. AND ARE AVAILABLE UPON REQUEST. ALTHOUGH ANY INFORMATION OR RECOMMENDATION CONTAINED HEREIN IS GIVEN IN GOOD FAITH, SELLER MAKES NO WARRANTY OR GUARANTEE, EXPRESS OR IMPLIED, (i) THAT THE RESULTS DESCRIBED HEREIN WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (ii) AS TO THE EFFECTIVENESS OR SAFETY OF ANY DESIGN INCORPORATING SELLER'S PRODUCTS, SERVICES OR RECOMMENDATIONS. EXCEPT AS PROVIDED IN SELLER'S STANDARD CONDITIONS OF SALE, SELLER SHALL NOT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS PRODUCTS OR SERVICES DESCRIBED HEREIN. Each user is responsible for making its own determination as to the suitability of Seller's products, services or recommendations for the user's particular use through appropriate end-use testing and analysis. Nothing in any document or oral statement shall be deemed to alter or waive any provision of Seller's Standard Conditions of Sale or this Disclaimer,unless it is specifically agreed to in a writing signed Seller. No statement Seller concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right of Seller or as a recommendation for the use of such product, service or design in a manner that infringes any patent or other intellectual property right.
SABIC Innovative Plastics is a trademark of SABIC Holding Europe B.V.

* Cycoloy is a trademark of SABIC Innovative Plastics IP BV

© 2012 SABIC Innovative Plastics Holding BV.All rights reserved

PC GS2020MR2 20%玻纤强化