- 产 品：PC/ABS LG9000 低光泽度,紫外稳定
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Cycoloy* Resin PC/ABS LG9000
PC+ABS blend, low gloss and UV-stable, suitable for automotive interior applications.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 550 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 75 | % | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 860 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 23500 | kgf/cm² | ASTM D 790 |
| Hardness,Rockwell R | 118 | - | ASTM D 785 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 54 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 32 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 414 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Total Energy,-30℃ | 345 | cm-kgf | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 129 | ℃ | ASTM D 1525 |
| HDT,0.45 MPa,3.2mm,unannealed | 123 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 107 | ℃ | ASTM D 648 |
| HDT,0.45 MPa,6.4mm,unannealed | 129 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,6.4mm,unannealed | 110 | ℃ | ASTM D 648 |
| CTE,-20℃ to 150℃,flow | 7.20E-05 | 1/℃ | ASTM E 831 |
| CTE,-20℃ to 150℃,xflow | 7.20E-05 | 1/℃ | ASTM E 831 |
| Thermal Conductivity | 0.2 | W/m-℃ | ASTM C 177 |
| Relative Temp Index,Elec | 60 | ℃ | UL 746B |
| Relative Temp Index,Mech w/impact | 60 | ℃ | UL 746B |
| Relative Temp Index,Mech w/o impact | 60 | ℃ | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.13 | - | ASTM D 792 |
| Water Absorption,24 hours | 0.1 | % | ASTM D 570 |
| Water Absorption,equilibrium,23C | 0.4 | % | ASTM D 570 |
| Mold Shrinkage,flow,3.2mm(5) | 0.5-0.7 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2mm(5) | 0.5-0.7 | % | SABIC Method |
| Melt Flow Rate,260℃/5.0 kgf | 17 | g/10 min | ASTM D 1238 |
| OPTICAL | Value | Unit | Standard |
| Gloss,untextured,60 degrees | 30 | - | ASTM D 523 |
| ELECTRICAL | Value | Unit | Standard |
| Arc Resistance,Tungsten{PLC} | 6 | PLC Code | ASTM D 495 |
| Hot Wire Ignition{PLC) | 2 | PLC Code | UL 746A |
| High Ampere Arc Ign,surface{PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index(UL){PLC} | 2 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94HB Flame Class Rating(3) | 1.49 | mm | UL 94 |
| Source GMD,last updated:2000/01/05 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 105-110 | ℃ |
| Drying Time | 3-4 | hrs |
| Drying Time(Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 275-300 | ℃ |
| Nozzle Temperature | 275-300 | ℃ |
| Front-Zone 3 Temperature | 260-300 | ℃ |
| Middle-Zone 2 Temperature | 255-295 | ℃ |
| Rear-Zone 1 Temperature | 250-290 | ℃ |
| Mold Temperature | 60-90 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 40-70 | rpm |
| Shot to Cylinder Size | 30-80 | % |
| Vent Depth | 0.038-0.076 | mm |
| Source GMD,last updated:2000/01/05 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.