PC/ABS C6600 标准流动,耐水解
  • 产 品:PC/ABS C6600 标准流动,耐水解
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Cycoloy™ Resin PC/ABS C6600
Nonbrominated, nonchlorinated FR PC+ABS with balanced flow, impact and hydrolytic stability for a wide variety of applications including business equipment, monitors, enclosures, among others.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 640 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 490 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 4 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 80 % ASTM D 638
Tensile Modulus,50mm/min 30500 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 950 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 26700 kgf/cm² ASTM D 790
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 56 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 520 cm-kgf ASTM D 3763
Instrumented Impact Total Energy,-30℃ 520 cm-kgf ASTM D 3763
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 99 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 83 ASTM D 648
HDT,0.45 MPa,6.4mm,unannealed 98 ASTM D 648
HDT,1.82 MPa,6.4mm,unannealed 90 ASTM D 648
Relative Temp Index,Elec 80 UL 746B
Relative Temp Index,Mech w/impact 70 UL 746B
Relative Temp Index,Mech w/o impact 80 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.19 - ASTM D 792
Water Absorption,24 hours 0.11 % ASTM D 570
Mold Shrinkage,flow,3.2mm(5) 0.4-0.6 % SABIC Method
Melt Flow Rate,260℃/2.16 kgf 21.5 g/10 min ASTM D 1238
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity,ROA >1.E+15 Ohm IEC 60093
Dielectric Strength,in oil,3.2mm 17 kV/mm IEC 60243-1
Relative Permittivity,1 MHz 2.7 - IEC 60250
Dissipation Factor,50/60 Hz 0.004 - IEC 60250
Dissipation Factor,1 MHz 0.006 - IEC 60250
Relative Permittivity,50/60 Hz 2.7 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-2 Flame Class Rating(3) 0.75 mm UL 94
UL Recognized,94V-0 Flame Class Rating(3) 1.5 mm UL 94
UL Recognized,94-5VB Rating(3) 2 mm UL 94
Source GMD,last updated:2005/07/25
Parameter Injection Molding Value Unit
Drying Temperature 80-90
Drying Time 3-4 hrs
Drying Time(Cumulative) 8 hrs
Maximum Moisture Content 0.04 %
Melt Temperature 245-275
Nozzle Temperature 245-275
Front-Zone 3 Temperature 245-275
Middle-Zone 2 Temperature 220-275
Rear-Zone 1 Temperature 220-255
Mold Temperature 60-80
Back Pressure 0.3-0.7 MPa
Screw Speed 40-70 rpm
Shot to Cylinder Size 30-80 %
Vent Depth 0.038-0.076 mm
Source GMD,last updated:2005/07/25

• NOTE: Back Pressure, Screw Speed, Shot to Cylinder Size and Vent Depth are only mentioned as general guidelines. These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding.

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.