- 产 品：PC/ABS CH6410 无溴无氯阻燃
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Cycoloy™ Resin PC/ABS CH6410
CH6410 is a high heat, impact modified PC resin, with nonbrominated, nonchlorinated flame retardant system. Limited colors only.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 640 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,50mm/min | 550 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,50mm/min | 5.5 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 88 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 25900 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 970 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 26500 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,50mm/min | 63 | MPa | ISO 527 |
| Tensile Stress,break,50mm/min | 55 | MPa | ISO 527 |
| Tensile Strain,yield,50mm/min | 5 | % | ISO 527 |
| Tensile Strain,break,50mm/min | 95 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2300 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 2400 | MPa | ISO 178 |
| Hardness,H358/30 | 100 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 92 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 740 | cm-kgf | ASTM D 3763 |
| Izod Impact,notched 80*10*4 +23℃ | 50 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 0℃ | 19 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 15 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 55 | kJ/m² | ISO 179/1eA |
| Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 127 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 118 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 7.74E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 5.94E-05 | 1/℃ | ASTM E 831 |
| CTE,23℃ to 60℃,flow | 7.00E-05 | 1/℃ | ISO 11359-2 |
| CTE,23℃ to 60℃,xflow | 7.00E-05 | 1/℃ | ISO 11359-2 |
| Ball Pressure Test,125℃ +/- 2℃ | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp,Rate B/50 | 134 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/120 | 135 | ℃ | ISO 306 |
| HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm | 126 | ℃ | ISO 75/Be |
| HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm | 113 | ℃ | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Mold Shrinkage on Tensile Bar,flow(2)(5) | 0.05-0.07 | % | SABIC Method |
| Mold Shrinkage,flow,3.2mm(5) | 0.4-0.5 | % | SABIC Method |
| Melt Flow Rate,260℃/2.16 kgf | 6.3 | g/10 min | ASTM D 1238 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Melt Volume Rate,MVR at 260℃/5.0 kg | 16 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity,ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength,in oil,3.2mm | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity,1 MHz | 2.7 | - | IEC 60250 |
| Dissipation Factor,50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor,1 MHz | 0.01 | - | IEC 60250 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Relative Permittivity,50/60 Hz | 2.7 | - | IEC 60250 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94V-1 Flame Class Rating(3) | 0.99 | mm | UL 94 |
| UL Recognized,94V-0 Flame Class Rating(3) | 1.49 | mm | UL 94 |
| Source GMD,last updated:2002/10/29 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 90-100 | ℃ |
| Drying Time | 2-4 | hrs |
| Drying Time(Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 270-300 | ℃ |
| Nozzle Temperature | 265-300 | ℃ |
| Front-Zone 3 Temperature | 265-300 | ℃ |
| Middle-Zone 2 Temperature | 260-300 | ℃ |
| Rear-Zone 1 Temperature | 260-300 | ℃ |
| Mold Temperature | 60-90 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 40-70 | rpm |
| Shot to Cylinder Size | 40-80 | % |
| Vent Depth | 0.038-0.076 | mm |
| Source GMD,last updated:2002/10/29 | ||
• NOTE: Back Pressure, Screw Speed, Shot to Cylinder Size and Vent Depth are only mentioned as general guidelines. These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding.
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【Cycoloy* Resin PC/ABS CH6410】