PC DE0021E 含炭纤维和阻燃剂.易成型
  • 产 品:PC DE0021E 含炭纤维和阻燃剂.易成型
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP STAT-KON* POLYCARBONATE COMPOUND
STRENGTH PLUS TAILORED ELECTRICAL PROPERTIES
Polycarbonate-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.

LNP™ STAT-KON™ Compound PC DE0021E 塑料物性表

Also known as:LNP™ Stat-kon™ Compound DC-1002 EM FR ECO
Product reorder name:DE0021E
LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Easy Molding.

MECHANICAL Value Unit Standard
Tensile Stress,break 1160 kgf/cm² ASTM D 638
Tensile Strain,break 1.8 % ASTM D 638
Tensile Modulus,50mm/min 93400 kgf/cm² ASTM D 638
Flexural Stress 1730 kgf/cm² ASTM D 790
Flexural Modulus 83800 kgf/cm² ASTM D 790
Tensile Stress,break 112 MPa ISO 527
Tensile Strain,break 2.1 % ISO 527
Tensile Modulus,1mm/min 9360 MPa ISO 527
Flexural Stress 169 MPa ISO 178
Flexural Modulus 8500 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 35 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 3 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 95 cm-kgf ASTM D 3763
Multiaxial Impact 77 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 31 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 7 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 93 ASTM D 648
CTE,-40℃ to 40℃,flow 1.67E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 6.08E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 1.67E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 6.09E-05 1/℃ ISO 11359-2
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 96 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.27 g/cm³ ASTM D 792
Mold Shrinkage,flow,24 hrs(5) 0.1-0.3 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.2-0.4 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.06-0.32 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.29-0.43 % ISO 294
Density 1.27 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.1 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+02-1.E+06 Ohm ASTM D 257
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94V-0 Flame Class Rating(3)(4) 1.5 mm UL 94 by SABIC-IP
Source GMD,last updated:2004/09/30
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4-6 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 255-290
Front-Zone 3 Temperature 260-270
Middle-Zone 2 Temperature 255-265
Rear-Zone 1 Temperature 250-260
Mold Temperature 40-65
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/09/30

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™ STAT-KON™ Compound PC DE0021E