- 产 品：PC DD0009PC 含碳粉和阻燃剂,是一个导电PC
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP STAT-KON* POLYCARBONATE COMPOUND
STRENGTH PLUS TAILORED ELECTRICAL PROPERTIES
Polycarbonate-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound PC DD0009PC 塑料物性表
Also known as:LNP™ Stat-kon™ Compound D-EP V-1 HP
Product reorder name:DD0009PC
LNP STAT-KON* DD0009PC is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yield | 630 | kgf/cm² | ASTM D 638 |
| Tensile Stress,break | 540 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yield | 4.9 | % | ASTM D 638 |
| Tensile Strain,break | 11 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 26700 | kgf/cm² | ASTM D 638 |
| Flexural Stress | 1030 | kgf/cm² | ASTM D 790 |
| Flexural Modulus | 28800 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield | 59 | MPa | ISO 527 |
| Tensile Stress,break | 51 | MPa | ISO 527 |
| Tensile Strain,yield | 4.6 | % | ISO 527 |
| Tensile Strain,break | 15.3 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2700 | MPa | ISO 527 |
| Flexural Stress | 98 | MPa | ISO 178 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 258 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 12 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Energy @ peak,23℃ | 156 | cm-kgf | ASTM D 3763 |
| Multiaxial Impact | 357 | cm-kgf | ISO 6603 |
| Izod Impact,unnotched 80*10*4 +23℃ | 137 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 11 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 140 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 128 | ℃ | ASTM D 648 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 130 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.29 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.14 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 0.8 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.8 | % | ASTM D 955 |
| Mold Shrinkage,flow,24 hrs(5) | 0.77 | % | ISO 294 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.79 | % | ISO 294 |
| Moisture Absorption(23℃/50% RH) | 0.23 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+02-1.E+06 | Ohm | ASTM D 257 |
| Source GMD,last updated:2004/09/30 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 120 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305-325 | ℃ |
| Front-Zone 3 Temperature | 320-330 | ℃ |
| Middle-Zone 2 Temperature | 310-320 | ℃ |
| Rear-Zone 1 Temperature | 295-305 | ℃ |
| Mold Temperature | 80-110 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2004/09/30 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【LNP™ STAT-KON™ Compound PC DD0009PC】