PC DF206XXH 含玻璃纤维和专有的润滑剂
  • 产 品:PC DF206XXH 含玻璃纤维和专有的润滑剂
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP* LUBRILOY* COMPOUND
LNP LUBRILOY RESIN ALL SERIES
LNP* Lubriloy* alloy composites provide lubrication through a unique, patented lubrication technology. Lubriloy* composites feature high impact and toughness and are used in a variety of demanding automotive, office equipment, electronics, and appliance applications. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ LUBRILOY™ Compound PC DF206XXH 塑料物性表

Also known as:LNP™ Lubriloy™ Compound DF-30 HC
Product reorder name:DF206XXH
LNP* Lubriloy* DF206XXH is a compound based on Polycarbonate containing Glass Fiber and Proprietary Lubricant. Added features include: Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 1140 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 2.6 % ASTM D 638
Tensile Modulus,5mm/min 88900 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 1770 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3mm/min,50mm span 1720 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 79800 kgf/cm² ASTM D 790
Tensile Stress,break,5mm/min 112 MPa ISO 527
Tensile Strain,break,5mm/min 2.6 % ISO 527
Tensile Modulus,1mm/min 8240 MPa ISO 527
Flexural Stress 166 MPa ISO 178
Flexural Modulus,2mm/min 7580 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 79 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 18 cm-kgf/cm ASTM D 256
Multiaxial Impact 66 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 266 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 49 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 17 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 146 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 142 ASTM D 648
CTE,-30℃ to 30℃,flow 5.60E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 5.10E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 145 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 141 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.4 - ASTM D 792
Density 1.39 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.11 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.4 - 0.6 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.5 - 0.7 % ASTM D 955
Wear Factor Washer 245 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Wear Factor Ring 27 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.49 - ASTM D 3702 Modified
Static COF 0.64 - ASTM D 3702 Modified
Moisture Absorption(23℃/50% RH) 0.16 % ISO 62
Source GMD,last updated:2012/03/26
Parameter Injection Molding Value Unit
Drying Temperature 100
Drying Time 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 305-315
Front-Zone 3 Temperature 305-315
Middle-Zone 2 Temperature 300-310
Rear-Zone 1 Temperature 295-305
Mold Temperature 65-95
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2012/03/26

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™ LUBRILOY™ Compound PC DF206XXH