Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.

Valox* Resin PBT IQ357 数据表
Valox* Resin IQ357: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 490 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 420 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 4.9 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 74 % ASTM D 638
Tensile Modulus,5mm/min 20400 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 760 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 21400 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 48 MPa ISO 527
Tensile Stress,break,50mm/min 40 MPa ISO 527
Tensile Strain,yield,50mm/min 4.6 % ISO 527
Tensile Strain,break,50mm/min 74.8 % ISO 527
Tensile Modulus,1mm/min 2190 MPa ISO 527
Flexural Stress,yield,2mm/min 73 MPa ISO 178
Flexural Modulus,2mm/min 2050 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 49 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 17 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 509 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*4 +23℃ 31 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 10 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 34 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 130 ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed 127 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 88 ASTM D 648
CTE,-40℃ to 40℃,flow 8.16E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 9.74E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 8.16E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 9.74E-05 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 130 ISO 306
Vicat Softening Temp,Rate B/120 133 ISO 306
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 122 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 84 ISO 75/Af
Relative Temp Index,Elec 120 UL 746B
Relative Temp Index,Mech w/impact 120 UL 746B
Relative Temp Index,Mech w/o impact 140 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.35 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 1.1-1.4 % SABIC Method
Melt Flow Rate,250℃/5.0 kgf 9.3 g/10 min ASTM D 1238
Density 1.32 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.08 % ISO 62
Moisture Absorption(23℃/50% RH) 0.08 % ISO 62
Melt Volume Rate,MVR at 250℃/5.0 kg 7 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Hot Wire Ignition{PLC) 2 PLC Code UL 746A
High Voltage Arc Track Rate{PLC} 4 PLC Code UL 746A
High Voltage Arc Resistance{PLC) 6 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 3 PLC Code UL 746A
Comparative Tracking Index(UL){PLC} 2 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94V-0 Flame Class Rating(3)(4) 0.63 mm UL 94 by SABIC-IP
UL Compliant,94-5VA Rating(3)(4) 3 mm UL 94 by SABIC-IP
Source GMD,last updated:2009/02/18
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time(Cumulative) 12 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-265
Nozzle Temperature 245-260
Front-Zone 3 Temperature 250-265
Middle-Zone 2 Temperature 245-260
Rear-Zone 1 Temperature 240-255
Mold Temperature 50-75
Back Pressure 0.3-0.7 MPa
Screw Speed 50-100 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.025-0.038 mm
Source GMD,last updated:2009/02/18

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.POM FT2010 晶须10的充填
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.