PBT HX420HP 玻璃30%填充,医疗食品级PBT
  • 产 品:PBT HX420HP 玻璃30%填充,医疗食品级PBT
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.

Valox* Resin PBT HX420HP 数据表
Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. Available in limited colors.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 1220 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 1220 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 3 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 3 % ASTM D 638
Tensile Modulus,5mm/min 94800 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 1920 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 77300 kgf/cm² ASTM D 790
Hardness,Rockwell R 118 - ASTM D 785
Tensile Stress,yield,5mm/min 125 MPa ISO 527
Tensile Stress,break,5mm/min 125 MPa ISO 527
Tensile Strain,yield,5mm/min 2 % ISO 527
Tensile Strain,break,5mm/min 2 % ISO 527
Tensile Modulus,1mm/min 9300 MPa ISO 527
Flexural Stress,yield,2mm/min 195 MPa ISO 178
Flexural Modulus,2mm/min 8500 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 81 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 8 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 8 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 101 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 45 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 45 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 8 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 7 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 5 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 215 ASTM D 1525
HDT,0.45 MPa,6.4mm,unannealed 215 ASTM D 648
HDT,1.82 MPa,6.4mm,unannealed 207 ASTM D 648
CTE,-40℃ to 40℃,flow 2.52E-05 1/℃ ASTM E 831
CTE,60℃ to 138℃,flow 2.52E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 2.50E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 1.20E-04 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 215 ISO 306
Vicat Softening Temp,Rate B/120 220 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 200 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.53 - ASTM D 792
Specific Volume 0.65 cm³/g ASTM D 792
Water Absorption,24 hours 0.06 % ASTM D 570
Mold Shrinkage,flow,3.2mm(5) 0.3-0.8 % SABIC Method
Mold Shrinkage,flow,1.5-3.2mm(5) 0.3-0.5 % SABIC Method
Mold Shrinkage,flow,3.2-4.6mm(5) 0.5-0.8 % SABIC Method
Mold Shrinkage,xflow,1.5-3.2mm(5) 0.4-0.6 % SABIC Method
Mold Shrinkage,xflow,3.2-4.6mm(5) 0.6-0.9 % SABIC Method
Melt Flow Rate,250℃/2.16 kgf 26 g/10 min ASTM D 1238
Density 1.53 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.26 % ISO 62
Moisture Absorption(23℃/50% RH) 0.06 % ISO 62
Melt Volume Rate,MVR at 250℃/2.16 kg 20 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Volume Resistivity >3.2E+16 Ohm-cm ASTM D 257
Dielectric Strength,in air,3.2mm 18.7 kV/mm ASTM D 149
Dielectric Strength,in oil,1.6mm 24.8 kV/mm ASTM D 149
Relative Permittivity,100 Hz 3.8 - ASTM D 150
Relative Permittivity,1 MHz 3.7 - ASTM D 150
Dissipation Factor,100 Hz 0.002 - ASTM D 150
Dissipation Factor,1 MHz 0.02 - ASTM D 150
Source GMD,last updated:2007/03/20
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time(Cumulative) 12 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-265
Nozzle Temperature 245-260
Front-Zone 3 Temperature 250-265
Middle-Zone 2 Temperature 245-260
Rear-Zone 1 Temperature 240-255
Mold Temperature 65-90
Back Pressure 0.3-0.7 MPa
Screw Speed 50-80 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.025-0.038 mm
Source GMD,last updated:2007/03/20

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.POM LO-21A 润滑剂系
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【Valox* Resin PBT HX420HP