PC FXE1414T 中等流动,韧性改进,加工优良
  • 产 品:PC FXE1414T 中等流动,韧性改进,加工优良
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Lexan* Visualfx* Resin
Beauty Is More Than Skin Deep
Lexan Polycarbonate Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Diamond, Luminescent, Diffusion, Lustre, and Edge Glow, as well as several metallic and natural material effects. Available in a variety of colors and base resins.

Lexan* Resin FXE1414T 英文物性表
Clear PC-siloxane copolymer with excellent processability, for Visual fX capability in "Energy" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.

Property
TYPICAL PROPERTIES(1)

MECHANICAL Value Unit  Standard 
Tensile Stress,yld,Type I,50mm/min 580 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 600 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 5.6 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 123.9 % ASTM D 638
Tensile Modulus,50mm/min 22300 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 930 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 22200 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 56 MPa ISO 527
Tensile Stress,break,50mm/min 55 MPa ISO 527
Tensile Strain,yield,50mm/min 5.4 % ISO 527
Tensile Strain,break,50mm/min 108.5 % ISO 527
Tensile Modulus,1mm/min 2300 MPa ISO 527
Flexural Stress,yield,2mm/min 88 MPa ISO 178
Flexural Modulus,2mm/min 2120 MPa ISO 178
IMPACT Value Unit  Standard 
Izod Impact,notched,23℃ 84 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 72 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 769 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*3 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*3 -30℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*3 +23℃ 65 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 55 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm 70 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm 60 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit  Standard 
Vicat Softening Temp,Rate A/50 138 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 120 ASTM D 648
CTE,-40℃ to 95℃,flow 6.70E-05 1/℃ ASTM E 831
CTE,-40℃ to 95℃,xflow 8.00E-05 1/℃ ASTM E 831
CTE,23℃ to 80℃,flow 6.70E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,xflow 8.00E-05 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ pass - IEC 60695-10-2
Vicat Softening Temp,Rate B/50 138 ISO 306
Vicat Softening Temp,Rate B/120 139 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 118 ISO 75/Af
PHYSICAL Value Unit  Standard 
Specific Gravity 1.19 - ASTM D 792
Mold Shrinkage,flow,3.2mm (5) 0.4-0.8 % SABIC Method
Melt Flow Rate,300℃/1.2 kgf 10 g/10 min ASTM D 1238
Density 1.19 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.13 % ISO 62
Moisture Absorption (23℃/50%RH) 0.09 % ISO 62
Melt Volume Rate,MVR at 300℃/1.2 kg 9 cm³/10 min ISO 1133
Source GMD,last updated:2004/11/19
Parameter Injection Molding Value Unit 
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295-315
Nozzle Temperature 290-310
Front-Zone 3 Temperature 295-315
Middle-Zone 2 Temperature 280-305
Rear-Zone 1 Temperature 215-295
Mold Temperature 70-95
Back Pressure 0.3-0.7 MPa
Screw Speed 40-70 rpm
Shot to Cylinder Size 40-60 %
Vent Depth 0.025-0.076 mm
Source GMD,last updated:2004/11/19

• NOTE: Back Pressure, Screw Speed, Shot to Cylinder Size and Vent Depth are only mentioned as general guidelines. These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding.

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
代理沙伯基础创新塑料(PC)聚碳酸酯材料