PC FXE1112T 耐低温负20度,钢琴黑,乌鸦黑
  • 产 品:PC FXE1112T 耐低温负20度,钢琴黑,乌鸦黑
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Lexan* Visualfx* Resin
Beauty Is More Than Skin Deep
Lexan Polycarbonate Visualfx Resins provide molded-in effects that can eliminate the need for modifications after molding. This can provide cleaner and more vibrant part aesthetics that will last as long as the part lasts. Visualfx Resins include Diamond, Luminescent, Diffusion, Lustre, and Edge Glow, as well as several metallic and natural material effects. Available in a variety of colors and base resins.

Lexan* Resin PC FXE1112T 英文数据物性表
Lexan* FXE1112T Lexan* polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. Lexan FXE1112T resin may be an excellent candidate for a broad range of applications. This product is available in GE Plastics' Visual fX* Piano Black, Raven Black & Illuminate color range only.

Property
TYPICALPROPERTIES(1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 590 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 580 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 5.7 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 117.9 % ASTM D 638
Tensile Modulus,50mm/min 23000 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 960 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 22900 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 57 MPa ISO 527
Tensile Stress,break,50mm/min 56 MPa ISO 527
Tensile Strain,yield,50mm/min 5.4 % ISO 527
Tensile Strain,break,50mm/min 119.4 % ISO 527
Tensile Modulus,1mm/min 2340 MPa ISO 527
Flexural Stress,yield,2mm/min 89 MPa ISO 178
Flexural Modulus,2mm/min 2140 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 75 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 63 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 763 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*3 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*3 -30℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*3 +23℃ 65 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 55 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm 65 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm 45 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate A/50 138 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 121 ASTM D 648
CTE,-40℃ to 95℃,flow 7.48E-05 1/℃ ASTM E 831
CTE,-40℃ to 95℃,xflow 7.64E-05 1/℃ ASTM E 831
CTE,23℃ to 80℃,flow 7.48E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,xflow 7.64E-05 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 138 ISO 306
Vicat Softening Temp,Rate B/120 139 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 116 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.19 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.4-0.8 % SABIC Method
Melt Flow Rate,300℃/1.2 kgf 20 g/10 min ASTM D 1238
Density 1.19 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.24 % ISO 62
Moisture Absorption(23℃/50% RH) 0.09 % ISO 62
Melt Volume Rate,MVR at 300℃/1.2 kg 19 cm³/10 min ISO 1133
Source GMD,last updated:2006/04/24
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time(Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295-315
Nozzle Temperature 290-310
Front-Zone 3 Temperature 295-315
Middle-Zone 2 Temperature 280-305
Rear-Zone 1 Temperature 270-295
Mold Temperature 70-95
Back Pressure 0.3-0.7 MPa
Screw Speed 40-70 rpm
Shot to Cylinder Size 40-60 %
Vent Depth 0.025-0.076 mm
Source GMD,last updated:2006/04/24

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.