- 产 品：PC BPL1000 高流动,抗冲击,无溴无氯阻燃
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Lexan* Non-Brominated and Non-Chlorinated Resin
Resins Intended to Meet Environmental Regulations
Flame retardant Lexan polycarbonate resins intended to meet government and voluntary standards, including global environmental regulations.
Lexan* Resin BPL1000 英文数据物性表
Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with UL-94 V0 rating at 0.8mm. Lexan BPL1000 resin offers various opaque color options and is ideal for thin wall applications.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 640 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,50mm/min | 520 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,50mm/min | 4.7 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 96.3 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 27300 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 1040 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 27100 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,50mm/min | 64 | MPa | ISO 527 |
| Tensile Stress,break,50mm/min | 53 | MPa | ISO 527 |
| Tensile Strain,yield,50mm/min | 4.7 | % | ISO 527 |
| Tensile Strain,break,50mm/min | 96.8 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2460 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 94 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 2360 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 61 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | N/A | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 495 | cm-kgf | ASTM D 3763 |
| Izod Impact,notched 80*10*4 +23℃ | 17 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 12 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 17 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 111 | ℃ | ASTM D 1525 |
| HDT,0.45 MPa,3.2mm,unannealed | 105 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 7.00E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 7.00E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 7.00E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 7.00E-05 | 1/℃ | ISO 11359-2 |
| Ball Pressure Test,75℃ +/- 2℃ | PASS | - | IEC 60695-10-2 |
| Vicat Softening Temp,Rate B/50 | 112 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/120 | 114 | ℃ | ISO 306 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 96 | ℃ | ISO 75/Af |
| Relative Temp Index,Elec | 80 | ℃ | UL 746B |
| Relative Temp Index,Mech w/impact | 80 | ℃ | UL 746B |
| Relative Temp Index,Mech w/o impact | 80 | ℃ | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.16 | - | ASTM D 792 |
| Mold Shrinkage on Tensile Bar,flow (2) (5) | 0.5-0.7 | % | SABIC Method |
| Mold Shrinkage,flow,3.2mm (5) | 0.5-0.7 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2mm (5) | 0.5-0.7 | % | SABIC Method |
| Melt Flow Rate,300℃/1.2 kgf | 25.2 | g/10 min | ASTM D 1238 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption,(23℃/sat) | 0.35 | % | ISO 62 |
| Moisture Absorption (23℃ / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate,MVR at 300℃/1.2 kg | 23 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Dielectric Strength,in oil,1.6mm | 27 | kV/mm | ASTM D 149 |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity,ROA | >1.E+15 | Ohm | IEC 60093 |
| Relative Permittivity,1 MHz | 2.9 | - | IEC 60250 |
| Dissipation Factor,50/60 Hz | 0.03 | - | IEC 60250 |
| Dissipation Factor,1 MHz | 0.01 | - | IEC 60250 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Relative Permittivity,50/60 Hz | 3 | - | IEC 60250 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94V-2 Flame Class Rating (3) | 0.45 | mm | UL 94 |
| UL Recognized,94V-0 Flame Class Rating (3) | 0.8 | mm | UL 94 |
| Glow Wire Flammability Index 960℃,passes at | 1 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature,1.0mm | 800 | ℃ | IEC 60695-2-13 |
| Oxygen Index (LOI) | 36 | % | ISO 4589 |
| Source GMD,last updated:2004/02/06 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 90 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 280-300 | ℃ |
| Nozzle Temperature | 270-290 | ℃ |
| Front-Zone 3 Temperature | 280-300 | ℃ |
| Middle-Zone 2 Temperature | 270-290 | ℃ |
| Rear-Zone 1 Temperature | 260-280 | ℃ |
| Hopper Temperature | 60-80 | ℃ |
| Mold Temperature | 90 | ℃ |
| Source GMD,last updated:2004/02/06 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
代理沙伯基础创新塑料（PC）聚碳酸酯材料