PC 955A 无氯无溴阻燃V0级,有透明和不透明颜色
  • 产 品:PC 955A 无氯无溴阻燃V0级,有透明和不透明颜色
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Lexan* Non-Brominated and Non-Chlorinated Resin
Resins Intended to Meet Environmental Regulations
Flame retardant Lexan polycarbonate resins intended to meet government and voluntary standards, including global environmental regulations.

Lexan* Resin 955A 英文数据物性表
Lexan* 955A Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating. Lexan 955A resin is available in transparent and tinted color options and is a general-purpose resin that is an excellent candidate for a wide variety of applications.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50 mm/min 630 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50 mm/min 680 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50 mm/min 6 % ASTM D 638
Tensile Strain,brk,Type I,50 mm/min 125 % ASTM D 638
Tensile Modulus,50 mm/min 23100 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 1020 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 24100 kgf/cm² ASTM D 790
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 81 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 805 cm-kgf ASTM D 3763
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 143 ASTM D 1525
HDT,0.45 MPa,3.2 mm,unannealed 137 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 126 ASTM D 648
CTE,-40℃ to 40℃,flow 6.84E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.38E-05 1/℃ ASTM E 831
Relative Temp Index,Elec 130 UL 746B
Relative Temp Index,Mech w/impact 120 UL 746B
Relative Temp Index,Mech w/o impact 130 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.19 - ASTM D 792
Mold Shrinkage,flow,3.2 mm(5) 0.6-0.8 % SABIC Method
Melt Flow Rate,300℃/1.2 kgf 7 g/10 min ASTM D 1238
ELECTRICAL Value Unit Standard
Arc Resistance,Tungsten{PLC} 7 PLC Code ASTM D 495
Hot Wire Ignition{PLC} 2 PLC Code UL 746A
High Voltage Arc Track Rate{PLC} 3 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 3 PLC Code UL 746A
Comparative Tracking Index(UL){PLC} 2 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-2 Flame Class Rating(3) 0.8 mm UL 94
UL Recognized,94V-0 Flame Class Rating(3) 3.04 mm UL 94
Glow Wire Flammability Index 960℃,passes at 1 mm IEC 60695-2-12
Glow Wire Ignitability Temperature,1.0 mm 875 IEC 60695-2-13
Source GMD,last updated:2008/04/29
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 290-320
Nozzle Temperature 280-310
Front-Zone 3 Temperature 290-320
Middle-Zone 2 Temperature 280-310
Rear-Zone 1 Temperature 270-300
Hopper Temperature 60-80
Mold Temperature 80-120
Source GMD,last updated:2008/04/29

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.