PC 505R 玻璃纤维10%填充,非氯溴阻燃V0级
  • 产 品:PC 505R 玻璃纤维10%填充,非氯溴阻燃V0级
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Lexan* Non-Brominated and Non-Chlorinated Resin
Resins Intended to Meet Environmental Regulations
Flame retardant Lexan polycarbonate resins intended to meet government and voluntary standards, including global environmental regulations.

Lexan* Resin 505R 英文数据物性表
Lexan* 505R Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. Lexan 505R contains non-chlorinated, non-brominated flame retardant systems with UL-94 V0 rating at 1.5mm. It is available in various opaque color options for high stiffness applications.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit  Standard 
Tensile Stress,yld,Type I,5 mm/min 640 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5 mm/min 480 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5 mm/min 3 % ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 12 % ASTM D 638
Tensile Modulus,5 mm/min 40000 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3 mm/min,50 mm span 1100 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 35900 kgf/cm² ASTM D 790
Taber Abrasion,CS-17,1 kg 11 mg/1000cy SABIC Method
Tensile Stress,yield,5 mm/min 60 MPa ISO 527
Tensile Stress,break,5 mm/min 45 MPa ISO 527
Tensile Strain,yield,5 mm/min 5 % ISO 527
Tensile Strain,break,5 mm/min 7 % ISO 527
Tensile Modulus,1 mm/min 3300 MPa ISO 527
Flexural Stress,yield,2 mm/min 95 MPa ISO 178
Flexural Modulus,2 mm/min 3400 MPa ISO 178
Hardness,H358/30 115 MPa ISO 2039-1
IMPACT Value Unit  Standard 
Izod Impact,unnotched,23℃ 163 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 10 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 8 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 622 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*3 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*3 -30℃ 130 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*3 +23℃ 10 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*3 -30℃ 8 kJ/m² ISO 180/1A
Izod Impact,unnotched 80*10*4 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 8 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 8 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*3 sp=62mm 10 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*3 sp=62mm 9 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 9 kJ/m² ISO 179/1eA
Charpy Impact,notched,23℃ 15 kJ/m² ISO 179/2C
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit  Standard 
Vicat Softening Temp,Rate B/50 149 ASTM D 1525
HDT,0.45 MPa,3.2 mm,unannealed 143 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 138 ASTM D 648
CTE,-40℃ to 40℃,flow 4.68E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 8.46E-05 1/℃ ASTM E 831
Thermal Conductivity 0.21 W/m-℃ ISO 8302
CTE,23℃ to 80℃,flow 4.00E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,xflow 7.00E-05 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate B/50 141 ISO 306
Vicat Softening Temp,Rate B/120 143 ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm 144 ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 136 ISO 75/Ae
HDT/Ae,1.8 MPa Annealed 120℃,2hrs 136 ISO 75/Ae
Relative Temp Index,Elec 130 UL 746B
Relative Temp Index,Mech w/impact 130 UL 746B
Relative Temp Index,Mech w/o impact 130 UL 746B
PHYSICAL Value Unit  Standard 
Specific Gravity 1.26 - ASTM D 792
Mold Shrinkage on Tensile Bar,flow (2) (5) 0.2-0.6 % SABIC Method
Mold Shrinkage,flow,3.2 mm (5) 0.5-0.7 % SABIC Method
Melt Flow Rate,300℃/1.2 kgf 7 g/10 min ASTM D 1238
Density 1.25 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.31 % ISO 62
Moisture Absorption (23℃ / 50% RH) 0.13 % ISO 62
Melt Volume Rate,MVR at 300℃/1.2 kg 7 cm³/10 min ISO 1133
ELECTRICAL Value Unit  Standard 
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity,ROA >1.E+15 Ohm IEC 60093
Dielectric Strength,in oil,0.8 mm 33 kV/mm IEC 60243-1
Dielectric Strength,in oil,1.6 mm 25 kV/mm IEC 60243-1
Dielectric Strength,in oil,3.2 mm 16 kV/mm IEC 60243-1
Relative Permittivity,1 MHz 2.8 - IEC 60250
Dissipation Factor,50/60 Hz 0.001 - IEC 60250
Dissipation Factor,1 MHz 0.01 - IEC 60250
Comparative Tracking Index 150 V IEC 60112
Relative Permittivity,50/60 Hz 2.9 - IEC 60250
FLAME CHARACTERISTICS Value Unit  Standard 
UL Recognized,94V-0 Flame Class Rating (3) 1.5 mm UL 94
UL Recognized,94-5VA Rating (3) 3 mm UL 94
Glow Wire Flammability Index 960℃,passes at 1 mm IEC 60695-2-12
Glow Wire Ignitability Temperature,1.0 mm 825 IEC 60695-2-13
Oxygen Index (LOI) 37 % ISO 4589
Source GMD,last updated:2008/09/30
Parameter Injection Molding Value Unit 
Drying Temperature 120
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 290-320
Nozzle Temperature 280-310
Front-Zone 3 Temperature 290-320
Middle-Zone 2 Temperature 280-310
Rear-Zone 1 Temperature 270-300
Hopper Temperature 60-80
Mold Temperature 80-120
Source GMD,last updated:2008/09/30

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.