Lexan* General Purpose Unfilled Resin
General Purpose Grades
General purpose materials provide a wide viscosity range with additional features like easy release, hydrolytic stability and UV stabilize grades. Various grades comply to food contact regulations and are available in a wide color range.
Lexan* Resin LI1911R 英文数据物性表
Low-viscosity multi-purpose PC having low levels of ionics species. Internal mold release.
Property
TYPICAL PROPERTIES (1)
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,50 mm/min | 630 | kgf/cm² | ASTM D 638 |
Tensile Stress,brk,Type I,50 mm/min | 700 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,50 mm/min | 7 | % | ASTM D 638 |
Tensile Strain,brk,Type I,50 mm/min | 125 | % | ASTM D 638 |
Tensile Modulus,5 mm/min | 24200 | kgf/cm² | ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span | 980 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3 mm/min,50 mm span | 23900 | kgf/cm² | ASTM D 790 |
Hardness,Rockwell R | 118 | - | ASTM D 785 |
Taber Abrasion,CS-17,1 kg | 10 | mg/1000cy | ASTM D 1044 |
Tensile Stress,yield,50 mm/min | 63 | MPa | ISO 527 |
Tensile Stress,break,50 mm/min | 65 | MPa | ISO 527 |
Tensile Strain,yield,50 mm/min | 6 | % | ISO 527 |
Tensile Strain,break,50 mm/min | 100 | % | ISO 527 |
Tensile Modulus,1 mm/min | 2350 | MPa | ISO 527 |
Flexural Stress,yield,2 mm/min | 90 | MPa | ISO 178 |
Flexural Modulus,2 mm/min | 2300 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 326 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 70 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Energy @ peak,23℃ | 633 | cm-kgf | ASTM D 3763 |
Izod Impact,notched 80*10*4 +23℃ | 12 | kJ/m² | ISO 180/1A |
Izod Impact,notched 80*10*4 -30℃ | 10 | kJ/m² | ISO 180/1A |
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp,Rate B/50 | 154 | ℃ | ASTM D 1525 |
HDT,1.82 MPa,3.2mm,unannealed | 125 | ℃ | ASTM D 648 |
HDT,0.45 MPa,6.4 mm,unannealed | 137 | ℃ | ASTM D 648 |
HDT,1.82 MPa,6.4 mm,unannealed | 129 | ℃ | ASTM D 648 |
CTE,-40℃ to 95℃,flow | 6.84E-05 | 1/℃ | ASTM E 831 |
Specific Heat | 1.25 | J/g-℃ | ASTM C 351 |
Thermal Conductivity | 0.19 | W/m-℃ | ASTM C 177 |
CTE,23℃ to 80℃,flow | 7.00E-05 | 1/℃ | ISO 11359-2 |
CTE,23℃ to 80℃,xflow | 7.00E-05 | 1/℃ | ISO 11359-2 |
Ball Pressure Test,75℃ +/- 2℃ | PASS | - | IEC 60695-10-2 |
Vicat Softening Temp,Rate B/50 | 140 | ℃ | ISO 306 |
Vicat Softening Temp,Rate B/120 | 141 | ℃ | ISO 306 |
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm | 122 | ℃ | ISO 75/Ae |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.2 | - | ASTM D 792 |
Specific Volume | 0.83 | cm³/g | ASTM D 792 |
Density | 1.19 | g/cm³ | ASTM D 792 |
Water Absorption,equilibrium,100℃ | 0.58 | % | ASTM D 570 |
Mold Shrinkage,flow,3.2 mm (5) | 0.5-0.7 | % | SABIC Method |
Melt Flow Rate,300℃/1.2 kgf | 17.5 | g/10 min | ASTM D 1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption,(23℃/sat) | 0.35 | % | ISO 62 |
Moisture Absorption (23℃/50% RH) | 0.15 | % | ISO 62 |
Melt Volume Rate,MVR at 220℃/5.0 kg | 21 | cm³/10 min | ISO 1133 |
OPTICAL | Value | Unit | Standard |
Light Transmission,2.54 mm | 88 | % | ASTM D 1003 |
Haze,2.54 mm | 1 | % | ASTM D 1003 |
Refractive Index | 1.586 | - | ASTM D 542 |
Source GMD,last updated:2004/08/03 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 120 | ℃ |
Drying Time | 3-4 | hrs |
Drying Time (Cumulative) | 48 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 280-305 | ℃ |
Nozzle Temperature | 275-300 | ℃ |
Front-Zone 3 Temperature | 280-305 | ℃ |
Middle-Zone 2 Temperature | 270-295 | ℃ |
Rear-Zone 1 Temperature | 260-280 | ℃ |
Mold Temperature | 70-95 | ℃ |
Back Pressure | 0.3-0.7 | MPa |
Screw Speed | 40-70 | rpm |
Shot to Cylinder Size | 40-60 | % |
Vent Depth | 0.025-0.076 | mm |
Source GMD,last updated:2004/08/03 |
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.