- 产 品：PC EM1210 优良的耐热,耐冲击,汽车内饰件用
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Lexan* General Purpose Unfilled Resin
General Purpose Grades
General purpose materials provide a wide viscosity range with additional features like easy release, hydrolytic stability and UV stabilize grades. Various grades comply to food contact regulations and are available in a wide color range.
Lexan* Resin EM1210 英文数据物性表
Automotive interiors. Excellent heat/impact resistance and outstanding property retention over wide temperature range/severe automotive conditions
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50 mm/min | 580 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,50 mm/min | 110 | % | ASTM D 638 |
| Flexural Stress,yld,1.3 mm/min,50 mm span | 820 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3 mm/min,50 mm span | 20700 | kgf/cm² | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 78 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 70 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,23℃,6.4mm | 70 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Energy @ peak,23℃ | 622 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Energy @ peak,-30 | 668 | cm-kgf | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,6.4 mm,unannealed | 135 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,6.4 mm,unannealed | 127 | ℃ | ASTM D 648 |
| CTE,-40℃ to 95℃,flow | 6.48E-05 | 1/℃ | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Water Absorption,24 hours | 0.16 | % | ASTM D 570 |
| Mold Shrinkage,flow,3.2 mm (5) | 0.5-0.7 | % | SABIC Method |
| Melt Flow Rate,300℃/1.2 kgf | 13 | g/10 min | ASTM D 1238 |
| Source GMD,last updated:2000/01/04 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 120 | ℃ |
| Drying Time | 3-4 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 295-315 | ℃ |
| Nozzle Temperature | 290-310 | ℃ |
| Front-Zone 3 Temperature | 295-315 | ℃ |
| Middle-Zone 2 Temperature | 280-305 | ℃ |
| Rear-Zone 1 Temperature | 270-295 | ℃ |
| Mold Temperature | 70-95 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 40-70 | rpm |
| Shot to Cylinder Size | 40-60 | % |
| Vent Depth | 0.025-0.076 | mm |
| Source GMD,last updated:2000/01/04 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.