- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
[Datasheet Makrolon 8345]数据
MVR (300 °C/1.2 kg) 3.0 cm³/10 min; 35 % glass fiber reinforced; high viscosity; easy release
☆These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Impact properties: N = non-break, P = partial break, C = complete break
ISO Shortname:ISO 7391-PC,GR,(,,)-05-3,GF35 | |||||
Property | Test Condition | Unit | Standard | Value | |
Rheological properties | |||||
☆ | Melt volume-flow rate | 300℃;1.2 kg | cm³/10 min | ISO 1133 | 3 |
. | Molding shrinkage,parallel/normal | 值的范围一般实践经验的基础上 | % | b.o.ISO 2577 | 0.3 - 0.5 |
. | Melt mass-flow rate | 300℃;1.2 kg | g/10 min | ISO 1133 | 3.5 |
Mechanical properties(23℃/50 % r.h.) | |||||
☆ | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 9400 |
☆ | Yield stress | 50 mm/min | MPa | ISO 527-1,-2 | 113 |
☆ | Yield strain | 50 mm/min | % | ISO 527-1,-2 | 1.9 |
☆ | Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 110 |
☆ | Strain at break | 5 mm/min | % | ISO 527-1,-2 | 1.8 |
☆ | Tensile creep modulus | 1 h | MPa | ISO 899-1 | 9000 |
☆ | Tensile creep modulus | 1000 h | MPa | ISO 899-1 | 8500 |
. | Flexural modulus | 2 mm/min | MPa | ISO 178 | 8600 |
. | Flexural strength | 2 mm/min | MPa | ISO 178 | 170 |
. | Flexural strain at flexural strength | 2 mm/min | % | ISO 178 | 2.5 |
☆ | Charpy impact strength | 23℃ | kJ/m² | ISO 179-1eU | 40C |
☆ | Charpy impact strength | -30℃ | kJ/m² | ISO 179-1eU | 45C |
. | Charpy notched impact strength | 23℃;3 mm | kJ/m² | ISO 7391/b.o.ISO 179-1eA | 8C |
. | Izod notched impact strength | 23℃;3.2 mm | kJ/m² | b.o.ISO 180-A | 8C |
☆ | Puncture maximum force | 23℃ | N | ISO 6603-2 | 900 |
☆ | Puncture maximum force | -30℃ | N | ISO 6603-2 | 900 |
☆ | Puncture energy | 23℃ | J | ISO 6603-2 | 5 |
☆ | Puncture energy | -30℃ | J | ISO 6603-2 | 5 |
. | Ball indentation hardness | . | N/mm² | ISO 2039-1 | 175 |
Thermal properties | |||||
☆ | Temperature of deflection under load | 1.80 MPa | ℃ | ISO 75-1,-2 | 140 |
☆ | Temperature of deflection under load | 0.45 MPa | ℃ | ISO 75-1,-2 | 144 |
☆ | Vicat softening temperature | 50 N;50℃/h | ℃ | ISO 306 | 148 |
. | Vicat softening temperature | 50 N;120℃/h | ℃ | ISO 306 | 149 |
☆ | 线性热膨胀系数,并行 | 23 to 55℃ | 10-4/K | ISO 11359-1,-2 | 0.2 |
☆ | 横向线性热膨胀系数 | 23 to 55℃ | 10-4/K | ISO 11359-1,-2 | 0.6 |
☆ | 燃烧性能UL94(1.5毫米)[UL认可] | 1.5 mm | Class | UL 94 | V-1 |
☆ | 燃烧性UL94 [UL认可] | 3.0 mm | Class | UL 94 | V-0 |
☆ | Oxygen index | Method A | % | ISO 4589-2 | 35 |
. | Thermal conductivity | 23℃ | W/(m·K) | ISO 8302 | 0.24 |
. | 耐热(球压试验) | . | ℃ | IEC 60695-10-2 | 136 |
. | 相对温度指数(拉伸强度)[UL认可] | 1.5 mm | ℃ | UL 746B | 125 |
. | 相对温度指数(拉伸冲击强度)[UL认可] | 1.5 mm | ℃ | UL 746B | 115 |
. | 相对温度指数(介电强度)[UL认可] | 1.5 mm | ℃ | UL 746B | 125 |
. | Glow wire test(GWFI) | 1.5 mm | ℃ | IEC 60695-2-12 | 960 |
. | Glow wire test(GWFI) | 3.0 mm | ℃ | IEC 60695-2-12 | 960 |
. | 来自小燃烧器的火焰中的应用 | Method K and F;2.0 mm | Class | DIN 53438-1,-3 | K1,F1 |
. | Needle flame test | Method K;1.5 mm | s | IEC 60695-11-5 | 60 |
. | Needle flame test | Method K;2.0 mm | s | IEC 60695-11-5 | 60 |
. | Needle flame test | Method K;3.0 mm | s | IEC 60695-11-5 | 120 |
. | Needle flame test | Method F;1.5 mm | s | IEC 60695-11-5 | 120 |
. | Needle flame test | Method F;2.0 mm | s | IEC 60695-11-5 | 120 |
. | Needle flame test | Method F;3.0 mm | s | IEC 60695-11-5 | 120 |
. | Burning rate(US-FMVSS) | >=1.0 mm | mm/min | ISO 3795 | passed |
. | Flash ignition temperature | . | ℃ | ASTM D1929 | 470 |
. | Self ignition temperature | . | ℃ | ASTM D1929 | 550 |
Electrical properties(23℃/50 % r.h.) | |||||
☆ | Relative permittivity | 100 Hz | - | IEC 60250 | 3.6 |
☆ | Relative permittivity | 1 MHz | - | IEC 60250 | 3.6 |
☆ | Dissipation factor | 100 Hz | 10-4 | IEC 60250 | 10 |
☆ | Dissipation factor | 1 MHz | 10-4 | IEC 60250 | 90 |
☆ | Volume resistivity | . | Ohm·m | IEC 60093 | 1E14 |
☆ | Surface resistivity | . | Ohm | IEC 60093 | 1E16 |
☆ | Electrical strength | 1 mm | kV/mm | IEC 60243-1 | 36 |
☆ | Comparative tracking index CTI | Solution A | Rating | IEC 60112 | 175 |
. | Comparative tracking index CTI M | Solution B | Rating | IEC 60112 | 125M |
. | Electrolytic corrosion | . | Rating | IEC 60426 | A1 |
Other properties(23℃) | |||||
☆ | Water absorption(saturation value) | Water at 23℃ | % | ISO 62 | 0.20 |
☆ | Water absorption(equilibrium value) | 23℃;50 % r.h. | % | ISO 62 | 0.10 |
☆ | Density | . | kg/m³ | ISO 1183-1 | 1480 |
. | Glass fiber content | Method A | % | b.o.ISO 3451-1 | 35 |
. | Bulk density | Pellets | kg/m³ | ISO 60 | 670 |
Processing conditions for test specimens | |||||
☆ | Injection molding-Melt temperature | . | ℃ | ISO 294 | 300 |
☆ | Injection molding-Mold temperature | . | ℃ | ISO 294 | 110 |
☆ | Injection molding-Injection velocity | . | mm/s | ISO 294 | 200 |