PC 2800 通用级,中等粘度
  • 产 品:PC 2800 通用级,中等粘度
  • 产 地:Bayer 拜耳
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

[Datasheet Makrolon 2800]数据
MVR (300 °C/1.2 kg) 10 cm³/10 min; general purpose; medium viscosity

☆These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Impact properties: N = non-break, P = partial break, C = complete break

ISO Shortname:ISO 7391-PC,M,(,,)-09-9
Property Test Condition Unit Standard Value
Rheological properties
Melt volume-flow rate 300℃;1.2 kg cm³/10 min ISO 1133 10
Molding shrinkage,parallel 60x60x2 mm;500 bar % ISO 294-4 0.65
Molding shrinkage,normal 60x60x2 mm;500 bar % ISO 294-4 0.7
. 成型收缩率,并行/正常 值的范围一般实践经验的基础上 % b.o.ISO 2577 0.6 - 0.8
. Melt mass-flow rate 300℃;1.2 kg g/10 min ISO 1133 10
Mechanical properties(23℃/50 % r.h.)
Tensile modulus 1 mm/min MPa ISO 527-1,-2 2350
Yield stress 50 mm/min MPa ISO 527-1,-2 65
Yield strain 50 mm/min % ISO 527-1,-2 6.3
Nominal strain at break 50 mm/min % ISO 527-1,-2 > 50
. Stress at break 50 mm/min MPa ISO 527-1,-2 75
. Strain at break 50 mm/min % b.o.ISO 527-1,-2 125
Tensile creep modulus 1 h MPa ISO 899-1 2200
Tensile creep modulus 1000 h MPa ISO 899-1 1900
. Flexural modulus 2 mm/min MPa ISO 178 2350
. Flexural strength 2 mm/min MPa ISO 178 96
. 抗折强度的弯曲应变 2 mm/min % ISO 178 7
. Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178 72
Charpy impact strength 23℃ kJ/m² ISO 179-1eU N
Charpy impact strength -30℃ kJ/m² ISO 179-1eU N
. Charpy impact strength -60℃ kJ/m² ISO 179-1eU N
. Charpy notched impact strength 23℃;3 mm kJ/m² ISO 7391/b.o.ISO 179-1eA 75P
. Charpy notched impact strength -30℃;3 mm kJ/m² ISO 7391/b.o.ISO 179-1eA 18C(P)
. Izod notched impact strength 23℃;3.2 mm kJ/m² b.o.ISO 180-A 85P
. Izod notched impact strength -30℃;3.2 mm kJ/m² b.o.ISO 180-A 16C
Puncture maximum force 23℃ N ISO 6603-2 5400
Puncture maximum force -30℃ N ISO 6603-2 6300
Puncture energy 23℃ J ISO 6603-2 60
Puncture energy -30℃ J ISO 6603-2 65
. Ball indentation hardness . N/mm² ISO 2039-1 113
Thermal properties
Glass transition temperature 10℃/min ISO 11357-1,-2 148
载荷下挠曲温度 1.80 MPa ISO 75-1,-2 128
载荷下挠曲温度 0.45 MPa ISO 75-1,-2 140
Vicat softening temperature 50 N;50℃/h ISO 306 147
. Vicat softening temperature 50 N;120℃/h ISO 306 148
线性热膨胀系数,并行 23 to 55℃ 10-4/K ISO 11359-1,-2 0.65
横向线性热膨胀系数 23 to 55℃ 10-4/K ISO 11359-1,-2 0.65
可燃烧的行为符合UL 94[UL认可] 0.75 mm Class UL 94 V-2
. 燃烧性UL94 [UL认可] 2.5 mm Class UL 94 HB
Oxygen index Method A % ISO 4589-2 27
. Thermal conductivity 23℃ W/(m·K) ISO 8302 0.20
. 耐热(球压试验) . IEC 60695-10-2 138
. 相对温度指数(拉伸强度)[UL认可] 1.5 mm UL 746B 125
. 相对温度指数(拉伸冲击强度)[UL认可] 1.5 mm UL 746B 115
. 相对温度指数(介电强度)[UL认可] 1.5 mm UL 746B 125
. Glow wire test(GWFI) 1.0 mm IEC 60695-2-12 850
. Glow wire test(GWFI) 1.5 mm IEC 60695-2-12 850
. Glow wire test(GWFI) 2.0 mm IEC 60695-2-12 850
. Glow wire test(GWFI) 3.0 mm IEC 60695-2-12 930
. Glow wire test(GWFI) 4.0 mm IEC 60695-2-12 960
. Glow wire test(GWIT) 1.0 mm IEC 60695-2-13 875
. Glow wire test(GWIT) 1.5 mm IEC 60695-2-13 875
. Glow wire test(GWIT) 2.0 mm IEC 60695-2-13 875
. Glow wire test(GWIT) 3.0 mm IEC 60695-2-13 875
. Glow wire test(GWIT) 4.0 mm IEC 60695-2-13 875
. Glow wire test 1.5 mm b.o.EDF HN60 E.02 750
. Glow wire test 3.0 mm b.o.EDF HN60 E.02 750
. Application of flame from small burner Method K and F;2.0 mm Class DIN 53438-1,-3 K1,F1
. Needle flame test Method K;1.5 mm s IEC 60695-11-5 5
. Needle flame test Method K;2.0 mm s IEC 60695-11-5 5
. Needle flame test Method K;3.0 mm s IEC 60695-11-5 10
. Needle flame test Method F;1.5 mm s IEC 60695-11-5 60
. Needle flame test Method F;2.0 mm s IEC 60695-11-5 60
. Needle flame test Method F;3.0 mm s IEC 60695-11-5 120
. Burning rate(US-FMVSS) >=1.0 mm mm/min ISO 3795 passed
. Flash ignition temperature . ASTM D1929 480
. Self ignition temperature . ASTM D1929 550
Electrical properties(23℃/50 % r.h.)
Relative permittivity 100 Hz - IEC 60250 3.1
Relative permittivity 1 MHz - IEC 60250 3.0
Dissipation factor 100 Hz 10-4 IEC 60250 5
Dissipation factor 1 MHz 10-4 IEC 60250 90
Volume resistivity . Ohm·m IEC 60093 1E14
Surface resistivity . Ohm IEC 60093 1E16
Electrical strength 1 mm kV/mm IEC 60243-1 34
Comparative tracking index CTI Solution A Rating IEC 60112 250
. Comparative tracking index CTI M Solution B Rating IEC 60112 125M
. Electrolytic corrosion . Rating IEC 60426 A1
Other properties(23℃)
吸水率(饱和值) Water at 23℃ % ISO 62 0.30
吸水性(平衡值) 23℃;50 % r.h. % ISO 62 0.12
Density . kg/m³ ISO 1183-1 1200
. Water vapor permeability 23℃;85 % RH;100 µm film g/(m²·24 h) ISO 15106-1 15
. Gas permeation Oxygen;100 µm film cm³/(m²·24 h·bar) b.o.ISO 2556 700
. Gas permeation Oxygen;25.4 µm(1 mil)film cm³/(m²·24 h·bar) b.o.ISO 2556 2760
. Gas permeation Nitrogen;100 µm film cm³/(m²·24 h·bar) b.o.ISO 2556 130
. Gas permeation Nitrogen;25.4 µm(1 mil)film cm³/(m²·24 h·bar) b.o.ISO 2556 510
. Gas permeation Carbon dioxide;100 µm film cm³/(m²·24 h·bar) b.o.ISO 2556 4300
. Gas permeation Carbon dioxide;25.4 µm(1 mil)film cm³/(m²·24 h·bar) b.o.ISO 2556 16900
. Bulk density Pellets kg/m³ ISO 60 660
Material specific properties
. Refractive index Procedure A - ISO 489 1.586
. Haze for transparent materials 3 mm % ISO 14782 < 0.8
. 光透射(透明材料) 1 mm % ISO 13468-2 89
光透射(透明材料) 2 mm % ISO 13468-2 89
. 光透射(透明材料) 3 mm % ISO 13468-2 88
. 光透射(透明材料) 4 mm % ISO 13468-2 87
Processing conditions for test specimens
Injection molding-Melt temperature . ISO 294 300
Injection molding-Mold temperature . ISO 294 80
Injection molding-Injection velocity . mm/s ISO 294 200