产品：PC 2408 MAS310 医疗设备,低粘度
产地：Bayer 拜耳
价格：电话报价
库存：20吨
交货：江苏苏州
苏州希普能：185 5121 3137 谭经理

上一篇：PC 2407 MAS145 低粘度,紫外线稳定,易释放下一篇：PC 2456 接触食品的质量,低粘度,易释放

[Datasheet Makrolon 2408 MAS310]
MVR (300 °C/1.2 kg) 23 cm³/10 min; medical devices; suitable for ETO and steam sterilization at 121 °C; biocompatible according to many ISO 10993-1 test requirements; low viscosity

☆These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Impact properties: N = non-break, P = partial break, C = complete break

ISO Shortname:ISO 7391-PC,M,(,,)-24-9
Property		Test Condition	Unit	Standard	Value
Rheological properties
☆	Melt volume-flow rate	300℃;1.2 kg	cm³/10 min	ISO 1133	23
☆	Molding shrinkage,parallel	60x60x2 mm;500 bar	%	ISO 294-4	0.65
☆	Molding shrinkage,normal	60x60x2 mm;500 bar	%	ISO 294-4	0.65
.	Melt mass-flow rate	300℃;1.2 kg	g/10 min	ISO 1133	24
Mechanical properties(23℃/50%r.h.)
☆	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	2350
☆	Yield stress	50 mm/min	MPa	ISO 527-1,-2	65
☆	Yield strain	50 mm/min	%	ISO 527-1,-2	6.3
☆	Nominal strain at break	50 mm/min	%	ISO 527-1,-2	> 50
.	Stress at break	50 mm/min	MPa	ISO 527-1,-2	70
.	Strain at break	50 mm/min	%	b.o.ISO 527-1,-2	120
.	Flexural modulus	2 mm/min	MPa	ISO 178	2350
.	Flexural strength	2 mm/min	MPa	ISO 178	96
.	抗折强度的弯曲应变	2 mm/min	%	ISO 178	7
.	Flexural stress at 3.5%strain	2 mm/min	MPa	ISO 178	72
☆	Charpy impact strength	23℃	kJ/m²	ISO 179-1eU	N
☆	Charpy impact strength	-30℃	kJ/m²	ISO 179-1eU	N
.	Charpy impact strength	-60℃	kJ/m²	ISO 179-1eU	N
.	Charpy notched impact strength	23℃;3 mm	kJ/m²	ISO 7391/b.o.ISO 179-1eA	65P
.	Charpy notched impact strength	-30℃;3 mm	kJ/m²	ISO 7391/b.o.ISO 179-1eA	14C
.	Izod notched impact strength	23℃;3.2 mm	kJ/m²	b.o.ISO 180-A	75P
.	Izod notched impact strength	-30℃;3.2 mm	kJ/m²	b.o.ISO 180-A	12C
☆	Puncture maximum force	23℃	N	ISO 6603-2	5100
☆	Puncture maximum force	-30℃	N	ISO 6603-2	6000
☆	Puncture energy	23℃	J	ISO 6603-2	55
☆	Puncture energy	-30℃	J	ISO 6603-2	65
Thermal properties
☆	Glass transition temperature	10℃/min	℃	ISO 11357-1,-2	147
☆	载荷下挠曲温度	1.80 MPa	℃	ISO 75-1,-2	127
☆	载荷下挠曲温度	0.45 MPa	℃	ISO 75-1,-2	139
☆	Vicat softening temperature	50 N;50℃/h	℃	ISO 306	147
.	Vicat softening temperature	50 N;120℃/h	℃	ISO 306	148
☆	线性热膨胀系数,并行	23 to 55℃	10-4/K	ISO 11359-1,-2	0.65
☆	横向线性热膨胀系数	23 to 55℃	10-4/K	ISO 11359-1,-2	0.65
.	Thermal conductivity	23℃	W/(m·K)	ISO 8302	0.20
.	Flash ignition temperature	.	℃	ASTM D1929	480
.	Self ignition temperature	.	℃	ASTM D1929	550
Other properties(23℃)
☆	吸水率(饱和值)	Water at 23℃	%	ISO 62	0.30
☆	吸水性(平衡值)	23℃;50 % r.h.	%	ISO 62	0.12
☆	Density	.	kg/m³	ISO 1183-1	1200
.	Bulk density	Pellets	kg/m³	ISO 60	660
Material specific properties
.	Refractive index	Procedure A	-	ISO 489	1.586
.	Haze for transparent materials	3 mm	%	ISO 14782	< 0.8
.	光透射(透明材料)	1 mm	%	ISO 13468-2	89
☆	光透射(透明材料)	2 mm	%	ISO 13468-2	89
.	光透射(透明材料)	3 mm	%	ISO 13468-2	88
.	光透射(透明材料)	4 mm	%	ISO 13468-2	87
Processing conditions for test specimens
☆	Injection molding-Melt temperature	.	℃	ISO 294	280
☆	Injection molding-Mold temperature	.	℃	ISO 294	80
☆	Injection molding-Injection velocity	.	mm/s	ISO 294	200