Datasheet Makrolon 2407 MAS070
MVR (300 °C/1.2 kg) 19 cm³/10 min; general purpose; low viscosity; UV stabilized; easy release

☆These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Impact properties: N = non-break, P = partial break, C = complete break

ISO Shortname:
Property		Test Condition	Unit	Standard	Value
Rheological properties
☆	Melt volume-flow rate	300℃;1.2 kg	cm³/10 min	ISO 1133	19
☆	Molding shrinkage,parallel	60x60x2 mm;500 bar	%	ISO 294-4	0.65
☆	Molding shrinkage,normal	60x60x2 mm;500 bar	%	ISO 294-4	0.7
	Molding shrinkage,parallel/normal	值的范围一般实践经验的基础上	%	b.o.ISO 2577	0.5-0.7
	Melt mass-flow rate	300℃;1.2 kg	g/10 min	ISO 1133	20
Mechanical properties(23℃/50 % r.h.)
☆	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	2400
☆	Yield stress	50 mm/min	MPa	ISO 527-1,-2	66
☆	Yield strain	50 mm/min	%	ISO 527-1,-2	6
☆	Nominal strain at break	50 mm/min	%	ISO 527-1,-2	> 50
	Stress at break	50 mm/min	MPa	ISO 527-1,-2	65
	Strain at break	50 mm/min	%	b.o.ISO 527-1,-2	120
☆	Tensile creep modulus	1 h	MPa	ISO 899-1	2200
☆	Tensile creep modulus	1000 h	MPa	ISO 899-1	1900
	Flexural modulus	2 mm/min	MPa	ISO 178	2350
	Flexural strength	2 mm/min	MPa	ISO 178	98
	Flexural strain at flexural strength	2 mm/min	%	ISO 178	7
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178	74
☆	Charpy impact strength	23℃	kJ/m²	ISO 179-1eU	N
☆	Charpy impact strength	-30℃	kJ/m²	ISO 179-1eU	N
	Charpy impact strength	-60℃	kJ/m²	ISO 179-1eU	N
	Charpy notched impact strength	23℃;3 mm	kJ/m²	ISO 7391/b.o.ISO 179-1eA	65P(C)
	Charpy notched impact strength	-30℃;3 mm	kJ/m²	ISO 7391/b.o.ISO 179-1eA	14C
	Izod notched impact strength	23℃;3.2 mm	kJ/m²	b.o.ISO 180-A	75P(C)
	Izod notched impact strength	-30℃;3.2 mm	kJ/m²	b.o.ISO 180-A	12C
☆	Puncture maximum force	23℃	N	ISO 6603-2	5100
☆	Puncture maximum force	-30℃	N	ISO 6603-2	6000
☆	Puncture energy	23℃	J	ISO 6603-2	55
☆	Puncture energy	-30℃	J	ISO 6603-2	65
	Ball indentation hardness		N/mm²	ISO 2039-1	116
Thermal properties
☆	Glass transition temperature	10℃/min	℃	ISO 11357-1,-2	143
☆	Temperature of deflection under load	1.80 MPa	℃	ISO 75-1,-2	124
☆	Temperature of deflection under load	0.45 MPa	℃	ISO 75-1,-2	136
☆	Vicat softening temperature	50 N;50℃/h	℃	ISO 306	143
	Vicat softening temperature	50 N;120℃/h	℃	ISO 306	145
☆	线性热膨胀系数，并行	23 to 55℃	10-4/K	ISO 11359-1,-2	0.65
☆	线性热膨胀系数，横向	23 to 55℃	10-4/K	ISO 11359-1,-2	0.65
☆	Burning behavior UL 94 [UL recognition]	0.75 mm	Class	UL 94	V-2
	Burning behavior UL 94 [UL recognition]	2.7 mm	Class	UL 94	HB
☆	Oxygen index	Method A	%	ISO 4589-2	27
	Thermal conductivity	23℃	W/(m·K)	ISO 8302	0.20
	Resistance to heat(ball pressure test)		℃	IEC 60695-10-2	135
	相对温度指数(拉伸强度)[UL认可]	1.5 mm	℃	UL 746B	125
	相对温度指数(拉伸冲击强度)[UL认可]	1.5 mm	℃	UL 746B	115
	相对温度指数(介电强度)[UL认可]	1.5 mm	℃	UL 746B	125
	Glow wire test(GWFI)	0.75 mm	℃	IEC 60695-2-12	850
	Glow wire test(GWFI)	1.5 mm	℃	IEC 60695-2-12	875
	Glow wire test(GWFI)	3.0 mm	℃	IEC 60695-2-12	930
	Glow wire test(GWIT)	0.75 mm	℃	IEC 60695-2-13	875
	Glow wire test(GWIT)	1.0 mm	℃	IEC 60695-2-13	875
	Glow wire test(GWIT)	1.5 mm	℃	IEC 60695-2-13	875
	Glow wire test(GWIT)	3.0 mm	℃	IEC 60695-2-13	875
	来自小燃烧器的火焰中的应用	Method K and F;2.0 mm	Class	DIN 53438-1,-3	K1,F1
	Needle flame test	Method K;1.5 mm	s	IEC 60695-11-5	5
	Needle flame test	Method K;2.0 mm	s	IEC 60695-11-5	5
	Needle flame test	Method K;3.0 mm	s	IEC 60695-11-5	10
	Needle flame test	Method F;1.5 mm	s	IEC 60695-11-5	60
	Needle flame test	Method F;2.0 mm	s	IEC 60695-11-5	120
	Needle flame test	Method F;3.0 mm	s	IEC 60695-11-5	120
	Burning rate(US-FMVSS)	>=1.0 mm	mm/min	ISO 3795	passed
	Flash ignition temperature		℃	ASTM D1929	480
	Self ignition temperature		℃	ASTM D1929	550
Electrical properties(23℃/50 % r.h.)
☆	Relative permittivity	100 Hz	-	IEC 60250	3.1
☆	Relative permittivity	1 MHz	-	IEC 60250	3.0
☆	Dissipation factor	100 Hz	10-4	IEC 60250	5
☆	Dissipation factor	1 MHz	10-4	IEC 60250	90
☆	Volume resistivity		Ohm·m	IEC 60093	1E14
☆	Surface resistivity		Ohm	IEC 60093	1E16
☆	Electrical strength	1 mm	kV/mm	IEC 60243-1	34
☆	Comparative tracking index CTI	Solution A	Rating	IEC 60112	250
	Comparative tracking index CTI M	Solution B	Rating	IEC 60112	125M
	Electrolytic corrosion		Rating	IEC 60426	A1
Other properties(23℃)
☆	Water absorption(saturation value)	Water at 23℃	%	ISO 62	0.30
☆	Water absorption(equilibrium value)	23℃;50 % r.h.	%	ISO 62	0.12
☆	Density		kg/m³	ISO 1183-1	1200
	Water vapor permeability	23℃;85 % RH;100 µm film	g/(m²·24 h)	ISO 15106-1	15
	Gas permeation	Oxygen;100 µm film	cm³/(m²·24 h·bar)	b.o.ISO 2556	800
	Gas permeation	Oxygen;25.4 µm(1 mil)film	cm³/(m²·24 h·bar)	b.o.ISO 2556	3150
	Gas permeation	Nitrogen;100 µm film	cm³/(m²·24 h·bar)	b.o.ISO 2556	160
	Gas permeation	Nitrogen;25.4 µm(1 mil)film	cm³/(m²·24 h·bar)	b.o.ISO 2556	630
	Gas permeation	Carbon dioxide;100 µm film	cm³/(m²·24 h·bar)	b.o.ISO 2556	4800
	Gas permeation	Carbon dioxide;25.4 µm(1 mil)film	cm³/(m²·24 h·bar)	b.o.ISO 2556	18900
	Bulk density	Pellets	kg/m³	ISO 60	660
Material specific properties
	Refractive index	Procedure A	-	ISO 489	1.584
	Haze for transparent materials	3 mm	%	ISO 14782	< 0.8
	光透射(透明材料)	1 mm	%	ISO 13468-2	89
☆	光透射(透明材料)	2 mm	%	ISO 13468-2	89
	光透射(透明材料)	3 mm	%	ISO 13468-2	88
	光透射(透明材料)	4 mm	%	ISO 13468-2	87
Processing conditions for test specimens
☆	Injection molding-Melt temperature	-	℃	ISO 294	280
☆	Injection molding-Mold temperature	-	℃	ISO 294	80
☆	Injection molding-Injection velocity	-	mm/s	ISO 294	200