LNP* Faradex* Compound
LNP Faradex Resin All Series
LNP* Faradex* compounds provide electromagnetic and radio frequency interference (EMI/RFI) attenuation in applications from electronics to material handling. Faradex compounds can also be used in applications where electrostatic discharge (ESD) is required. Faradex* compounds provide mechanical properties, part weight and a design freedom similar to standard unfilled base resins. LNP* specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™ Faradex™ Compound PBT WX94736 塑料物性
Also known as:LNP™Faradex™Compound PDX-W-94736
Product reorder name:WX94736
LNP* Faradex* WX94736 is a compound based on Polybutylene Terephalate resin containing Stainless Steel.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yield | 540 | kgf/cm² | ASTM D 638 |
Tensile Stress,break | 540 | kgf/cm² | ASTM D 638 |
Tensile Strain,yield | 2.7 | % | ASTM D 638 |
Tensile Strain,break | 2.8 | % | ASTM D 638 |
Tensile Modulus,50mm/min | 35100 | kgf/cm² | ASTM D 638 |
Flexural Stress | 560 | kgf/cm² | ASTM D 790 |
Flexural Modulus | 28100 | kgf/cm² | ASTM D 790 |
Tensile Stress,yield | 53 | MPa | ISO 527 |
Tensile Stress,break | 53 | MPa | ISO 527 |
Tensile Strain,yield | 2.8 | % | ISO 527 |
Tensile Strain,break | 2.9 | % | ISO 527 |
Tensile Modulus,1mm/min | 3110 | MPa | ISO 527 |
Flexural Stress | 83 | MPa | ISO 178 |
Flexural Modulus | 3100 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 62 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 5 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Energy @ peak,23℃ | 63 | cm-kgf | ASTM D 3763 |
Multiaxial Impact | 19 | cm-kgf | ISO 6603 |
Izod Impact,unnotched 80*10*4 +23℃ | 22 | kJ/m² | ISO 180/1U |
Izod Impact,notched 80*10*4 +23℃ | 6 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
HDT,0.45 MPa,3.2mm,unannealed | 143 | ℃ | ASTM D 648 |
HDT,1.82 MPa,3.2mm,unannealed | 99 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 8.28E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,xflow | 6.84E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,flow | 8.30E-05 | 1/℃ | ISO 11359-2 |
CTE,-40℃ to 40℃,xflow | 6.90E-05 | 1/℃ | ISO 11359-2 |
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 147 | ℃ | ISO 75/Bf |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 123 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Density | 1.51 | g/cm³ | ASTM D 792 |
Moisture Absorption,50% RH,24 hrs | 0.1 | % | ASTM D 570 |
Mold Shrinkage,flow,24 hrs(5) | 0.8-1 | % | ASTM D 955 |
Mold Shrinkage,xflow,24 hrs(5) | 1-1.2 | % | ASTM D 955 |
Mold Shrinkage,flow,24 hrs(5) | 0.89 | % | ISO 294 |
Mold Shrinkage,xflow,24 hrs(5) | 1.1 | % | ISO 294 |
Density | 1.5 | g/cm³ | ISO 1183 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | 3.E+00-7.E+00 | Ohm-cm | ASTM D 257 |
Surface Resistivity | 2.E+00-6.E+00 | Ohm | ASTM D 257 |
Source GMD,last updated:2008/09/24 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 120 | ℃ |
Drying Time | 4 | hrs |
Maximum Moisture Content | 0.05 | % |
Melt Temperature | 240-265 | ℃ |
Front-Zone 3 Temperature | 260-270 | ℃ |
Middle-Zone 2 Temperature | 245-255 | ℃ |
Rear-Zone 1 Temperature | 220-230 | ℃ |
Mold Temperature | 80-100 | ℃ |
Back Pressure | 0.2-0.3 | MPa |
Screw Speed | 30-60 | rpm |
Source GMD,last updated:2008/09/24 |
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.PA66 103FHS BKB009 热稳定,润滑,快速周期