PBT VR4860 玻璃35%填充,阻燃PBT
  • 产 品:PBT VR4860 玻璃35%填充,阻燃PBT
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.

Valox* Resin PBT VR4860 数据表
35% Glass filled PBT, Flame Retardant, UL Recognized, Utility grade, Black color only

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 980 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 1680 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 70300 kgf/cm² ASTM D 790
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 43 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 5 cm-kgf/cm ASTM D 256
THERMAL Value Unit Standard
HDT,1.82 MPa,6.4mm,unannealed 187 ASTM D 648
Relative Temp Index,Elec 120 UL 746B
Relative Temp Index,Mech w/impact 120 UL 746B
Relative Temp Index,Mech w/o impact 120 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.65 - ASTM D 792
Specific Volume 0.61 cm³/g ASTM D 792
Water Absorption,24 hours 0.06 % ASTM D 570
Mold Shrinkage,flow,1.5-3.2mm(5) 0.3-0.5 % SABIC Method
Mold Shrinkage,flow,3.2-4.6mm(5) 0.5-0.8 % SABIC Method
Mold Shrinkage,xflow,1.5-3.2mm(5) 0.4-0.6 % SABIC Method
Mold Shrinkage,xflow,3.2-4.6mm(5) 0.6-0.9 % SABIC Method
ELECTRICAL Value Unit Standard
Volume Resistivity 1.50E+16 Ohm-cm ASTM D 257
Relative Permittivity,100 Hz 3.9 - ASTM D 150
Dissipation Factor,100 Hz 0.002 - ASTM D 150
Arc Resistance,Tungsten{PLC} 7 PLC Code ASTM D 495
Hot Wire Ignition{PLC) 0 PLC Code UL 746A
High Voltage Arc Track Rate{PLC} 3 PLC Code UL 746A
High Ampere Arc Ign,surface{PLC} 2 PLC Code UL 746A
Comparative Tracking Index(UL){PLC} 3 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94V-2 Flame Class Rating(3) 0.71 mm UL 94
UL Recognized,94V-0 Flame Class Rating(3) 1.47 mm UL 94
UL Recognized,94-5VA Rating(3) 2.51 mm UL 94
Source GMD,last updated:2011/08/23
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time (Cumulative) 12 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-265
Nozzle Temperature 245-260
Front-Zone 3 Temperature 250-265
Middle-Zone 2 Temperature 245-260
Rear-Zone 1 Temperature 240-255
Mold Temperature 65-90
Back Pressure 0.3-0.7 MPa
Screw Speed 50-80 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.025-0.038 mm
Source GMD,last updated:2011/08/23

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.SBS报价
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【Valox* Resin PBT VR4860