PBT SHF436HR 超高流量,玻纤30%增强,耐水解耐磨
  • 产 品:PBT SHF436HR 超高流量,玻纤30%增强,耐水解耐磨
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.

Valox* Resin PBT SHF436HR 数据表
PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 1130 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 1130 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 2 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 2 % ASTM D 638
Tensile Modulus,5mm/min 121300 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 1660 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 88700 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 117 MPa ISO 527
Tensile Stress,break,5mm/min 117 MPa ISO 527
Tensile Strain,yield,5mm/min 2 % ISO 527
Tensile Strain,break,5mm/min 2 % ISO 527
Tensile Modulus,1mm/min 9490 MPa ISO 527
Flexural Stress,yield,2mm/min 165 MPa ISO 178
Flexural Modulus,2mm/min 7720 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 9 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 9 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 61 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*4 +23℃ 8 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 8 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 8 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 200 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 214 ASTM D 648
CTE,-40℃ to 40℃,flow 1.00E-04 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 3.00E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 1.00E-04 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 3.00E-05 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 200 ISO 306
Vicat Softening Temp,Rate B/120 200 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 206 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.53 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.3-0.5 % SABIC Method
Melt Flow Rate,250℃/2.16 kgf 30 g/10 min ASTM D 1238
Density 1.53 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.28 % ISO 62
Moisture Absorption(23℃/50% RH) 0.06 % ISO 62
Melt Volume Rate,MVR at 250℃/2.16 kg 30 cm³/10 min ISO 1133
Source GMD,last updated:2006/10/18
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time(Cumulative) 12 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-265
Nozzle Temperature 245-260
Front-Zone 3 Temperature 250-265
Middle-Zone 2 Temperature 245-260
Rear-Zone 1 Temperature 240-255
Mold Temperature 65-90
Back Pressure 0.3-0.7 MPa
Screw Speed 50-80 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.025-0.038 mm
Source GMD,last updated:2006/10/18

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.PPO WCD801A 无卤挤出,阻燃,电线绝缘和电缆护套用
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.