- 产 品：PBT FXV310SK 未增强PBT树脂,很高的流动特性
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.
Valox* Resin PBT FXV310SK 数据表
VALOX FXV310SK is an unreinforced PBT injection moulding Visualfx* resin with high flow characteristics and containing a metal sparkle. Applications: automotive bezels and appliances.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 560 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,50mm/min | 170 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,50mm/min | 20 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 100 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 27500 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 900 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 24500 | kgf/cm² | ASTM D 790 |
| Taber Abrasion,CS-17,1 kg | 9 | mg/1000cy | SABIC Method |
| Tensile Stress,yield,50mm/min | 60 | MPa | ISO 527 |
| Tensile Stress,break,50mm/min | 58 | MPa | ISO 527 |
| Tensile Strain,yield,50mm/min | 7 | % | ISO 527 |
| Tensile Strain,break,50mm/min | 15 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2750 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 2750 | MPa | ISO 178 |
| Hardness,H358/30 | 85 | MPa | ISO 2039-1 |
| Hardness,Rockwell R | 117 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 4 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 5 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 571 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*4 +23℃ | NB | kJ/m² | ISO 180/1U |
| Izod Impact,unnotched 80*10*4 -30℃ | NB | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 5 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 5 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| Charpy Impact,notched,23℃ | 3 | kJ/m² | ISO 179/2C |
| Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
| Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 185 | ℃ | ASTM D 1525 |
| HDT,1.82 MPa,3.2mm,unannealed | 55 | ℃ | ASTM D 648 |
| CTE,-20℃ to 150℃,xflow | 1.30E-04 | 1/℃ | ASTM E 831 |
| CTE,0℃ to 100℃,flow | 1.30E-04 | 1/℃ | ASTM E 831 |
| Thermal Conductivity | 0.16 | W/m-℃ | ISO 8302 |
| Ball Pressure Test,125℃ +/- 2℃ | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp,Rate B/50 | 185 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/120 | 187 | ℃ | ISO 306 |
| HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm | 160 | ℃ | ISO 75/Be |
| HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm | 55 | ℃ | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.31 | - | ASTM D 792 |
| Mold Shrinkage,flow,3.2mm(5) | 1.9-2.4 | % | SABIC Method |
| Melt Flow Rate,250℃/2.16 kgf | 27.5 | g/10 min | ASTM D 1238 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Water Absorption,(23℃/sat) | 0.34 | % | ISO 62 |
| Moisture Absorption(23℃/50% RH) | 0.08 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity,ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength,in oil,3.2mm | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity,1 MHz | 3.1 | - | IEC 60250 |
| Dissipation Factor,50/60 Hz | 0.002 | - | IEC 60250 |
| Dissipation Factor,1 MHz | 0.02 | - | IEC 60250 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Relative Permittivity,50/60 Hz | 3.3 | - | IEC 60250 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant,94HB Flame Class Rating(3)(4) | 1.47 | mm | UL 94 by SABIC-IP |
| UL Compliant,94HB Flame Class Rating 2nd value(3)(4) | 3.12 | mm | UL 94 by SABIC-IP |
| Oxygen Index(LOI) | 20 | % | ISO 4589 |
| Source GMD,last updated:2010/05/19 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 110-120 | ℃ |
| Drying Time | 2-4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250-270 | ℃ |
| Nozzle Temperature | 240-260 | ℃ |
| Front-Zone 3 Temperature | 245-265 | ℃ |
| Middle-Zone 2 Temperature | 240-255 | ℃ |
| Rear-Zone 1 Temperature | 230-245 | ℃ |
| Hopper Temperature | 40-60 | ℃ |
| Mold Temperature | 40-100 | ℃ |
| Source GMD,last updated:2010/05/19 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.POM 588P NC010 中高粘,热稳定,尺寸稳定
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【Valox* Resin PBT FXV310SK】