PBT EH7020 矿物填充,金属化
  • 产 品:PBT EH7020 矿物填充,金属化
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.

Valox* Resin PBT EH7020 数据表
MINERAL FILLED, METALLIZABLE

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 590 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 1050 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 42100 kgf/cm² ASTM D 790
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 39 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 3 cm-kgf/cm ASTM D 256
THERMAL Value Unit Standard
HDT,0.45 MPa,6.4mm,unannealed 187 ASTM D 648
HDT,1.82 MPa,6.4mm,unannealed 105 ASTM D 648
CTE,-40℃ to 40℃,flow 5.58E-05 1/℃ ASTM E 831
PHYSICAL Value Unit Standard
Specific Gravity 1.49 - ASTM D 792
Mold Shrinkage,flow,1.5-3.2mm(5) 1.4-1.6 % SABIC Method
Mold Shrinkage,flow,3.2-4.6mm(5) 1.5-1.6 % SABIC Method
Mold Shrinkage,xflow,1.5-3.2mm(5) 1.3-1.4 % SABIC Method
Mold Shrinkage,xflow,3.2-4.6mm(5) 1.4-1.5 % SABIC Method
ELECTRICAL Value Unit Standard
Dielectric Strength,in oil,3.2mm 16.9 kV/mm ASTM D 149
Relative Permittivity,50/60 Hz 3.1 - ASTM D 150
Relative Permittivity,1 MHz 2.9 - ASTM D 150
Dissipation Factor,50/60 Hz 0.0039 - ASTM D 150
Dissipation Factor,1 MHz 0.014 - ASTM D 150
Source GMD,last updated:2012/04/17
Parameter Injection Molding Value Unit
Drying Temperature 120
Drying Time 3-4 hrs
Drying Time(Cumulative) 12 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250-265
Nozzle Temperature 245-260
Front-Zone 3 Temperature 250-265
Middle-Zone 2 Temperature 245-260
Rear-Zone 1 Temperature 240-255
Mold Temperature 65-90
Back Pressure 0.3-0.7 MPa
Screw Speed 50-80 rpm
Shot to Cylinder Size 40-80 %
Vent Depth 0.025-0.038 mm
Source GMD,last updated:2012/04/17

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards. PC/ABS C3650 无溴无氯阻燃,高冲击,耐热
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【Valox* Resin PBT EH7020