PBT 7062HP FDA认证,38%矿物填充
  • 产 品:PBT 7062HP FDA认证,38%矿物填充
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Valox* Resin
Valox* Resin All Series
The Valox* family of thermoplastic polyester resins are semi-crystalline materials based on polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) polymers. Valox resins are highly tailorable, combining heat, chemical resistance, and outstanding electrical properties with exceptionally good processability and surface appearance.

Valox* Resin PBT 7062HP 数据表
ENDURAN 7062HP is a 38% mineral filled & FDA compliance injection moulding resin.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 540 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 560 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 3 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 3 % ASTM D 638
Tensile Modulus,5mm/min 42000 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 1120 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 45600 kgf/cm² ASTM D 790
Taber Abrasion,CS-17,1 kg 74 mg/1000cy SABIC Method
Tensile Stress,yield,5mm/min 60 MPa ISO 527
Tensile Stress,break,5mm/min 60 MPa ISO 527
Tensile Strain,yield,5mm/min 3 % ISO 527
Tensile Strain,break,5mm/min 3 % ISO 527
Tensile Modulus,1mm/min 4200 MPa ISO 527
Flexural Stress,break,2mm/min 100 MPa ISO 178
Flexural Modulus,2mm/min 3900 MPa ISO 178
Hardness,H358/30 140 MPa ISO 2039-1
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 43 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 2 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 2 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 50 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 30 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 30 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 3 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 3 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 2 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 2 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm 37 kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm 33 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 175 ASTM D 1525
HDT,1.82 MPa,3.2mm,unannealed 69 ASTM D 648
CTE,-40℃ to 40℃,flow 9.00E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 9.00E-05 1/℃ ASTM E 831
Thermal Conductivity 0.32 W/m-℃ ISO 8302
CTE,23℃ to 80℃,flow 9.00E-05 1/℃ ISO 11359-2
CTE,23℃ to 80℃,xflow 9.00E-05 1/℃ ISO 11359-2
CTE,23℃ to 150℃,flow 1.10E-04 1/℃ ISO 11359-2
CTE,23℃ to 150℃,xflow 1.10E-04 1/℃ ISO 11359-2
Ball Pressure Test,125℃+/-2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate A/50 215 ISO 306
Vicat Softening Temp,Rate B/50 175 ISO 306
Vicat Softening Temp,Rate B/120 175 ISO 306
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 65 ISO 75/Ae
PHYSICAL Value Unit Standard
Specific Gravity 1.81 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 1.2-1.9 % SABIC Method
Melt Flow Rate,266℃/1.2 kgf 33 g/10 min ASTM D 1238
Density 1.81 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.07 % ISO 62
Moisture Absorption(23℃/50% RH) 0.07 % ISO 62
Melt Volume Rate,MVR at 265℃/1.2 kg 21 cm³/10 min ISO 1133
Melt Volume Rate,MVR at 265℃/2.16 kg 41 cm³/10 min ISO 1133
Source GMD,last updated:2006/10/11
Parameter Injection Molding Value Unit
Drying Temperature 110-120
Drying Time 2-4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 255-280
Nozzle Temperature 245-270
Front-Zone 3 Temperature 250-270
Middle-Zone 2 Temperature 240-260
Rear-Zone 1 Temperature 230-250
Hopper Temperature 40-60
Mold Temperature 60-100
Source GMD,last updated:2006/10/11

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【Valox* Resin PBT 7062HP