- 产 品：PBT HR5315HF NC010 GF15%,抗水解,耐冲击
- 产 地：DuPont 杜邦
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
杜邦™CRASTIN®PBT
热塑性聚酯树脂
PBT玻璃纤维增强树脂
Crastin® HR5315HF NC010 is a 15% glass reinforced PBT with high flow (HF), moderately toughened, hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and impact resistance. Developed for USCAR Class 3 and 4 environments.
CRASTIN的®HR5315HF NC010 是15%玻璃纤维增强树脂与高流量（高频），中度钢化玻璃，抗水解（HR）树脂。出色的平衡性能的终端撤军和耐冲击性。制定USCAR第3级和4环境。
|
Property
|
Test Method
|
Units
|
Value
|
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PBT-IGF15
>PBT-IGF15<
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Flexural Strength
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
95 (13.8)
3
5200 (750)
4700 (680)
150 (21.8)
7
10
30
60
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Parallel
23 - 55°C (73 - 130°F)
CLTE, Normal
23 - 55°C (73 - 130°F)
Glass Transition Temperature
10°C/min
Thermal Conductivity
Specific Heat
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 11357-1/-2
ISO 11357-4
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
°C (°F)
2
W/m K (Btu in/h ft F)
J/kg K (Btu/lb F)
|
220 (430)
200 (390)
225 (437)
0.41 (0.23)
1.1 (0.61)
65 (149)
0.26 (1.8)
1860 (0.44)
|
|
Rheological
Melt Volume-Flow Rate
|
ISO 1133
|
3
cm /10 min (ml/10 min)
|
18
|
|
Electrical
Volume Resistivity
Dissipation Factor
1E2 Hz
1E6 Hz
CTI
|
IEC 60093
IEC 60250
IEC 60112
|
ohm m
E-4
V
|
>1E13
100
100
325
|
|
Flammability
Flammability Classification
1.5mm
Oxygen Index
|
IEC 60695-11-10
ISO 4589-1/-2
|
%
|
HB
20
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Other
Density
Hardness, Rockwell
Scale R
Water Absorption
Equilibrium 50%RH, 1.0mm
Saturation, immersed, 1.0mm
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 2039/2
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m (g/cm )
%
%
|
1370 (1.37)
115
0.15
0.4
1.1
0.5
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
|
240-260 (465-500)
250 (480)
30-130 (85-265)
80 (175)
2-4
110-130 (230-265)
<0.04
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Crastin® are trademarks or registered trademarks of DuPont Company. Copyright© 2011