- 产 品：PBT FG6129 NC010 非增强型,高粘度
- 产 地：DuPont 杜邦
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
杜邦™CRASTIN®PBT
热塑性聚酯树脂
非增强树脂
Crastin® FG6129 NC010 is an unreinforced, high viscosity polybutylene terephthalate resin for extrusion and injection molding. It has been developed for consideration into applications such as parts for the food industry.
CRASTIN®FG6129 NC010非增强型，高粘度聚对苯二甲酸乙二醇酯树脂的挤出和注射成型。它已经发展到应用，如食品行业的零部件审议。
|
Property
|
Test Method
|
Units
|
Value
|
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PBT
>PBT<
|
|
Mechanical
Yield Stress
Yield Strain
Strain at Break
50mm/min
Nominal Strain at Break
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Flexural Modulus
Flexural Strength
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 899
ISO 178
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
%
%
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
58 (8.4)
5
200
>50
2600 (377)
2600 (377)
1800 (261)
2350 (340)
85 (12.3)
4
5.5
N
N
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Thermal
Deflection Temperature
0.45MPa
0.45MPa, Annealed
1.80MPa
1.80MPa, Annealed
Melting Temperature
10°C/min
CLTE, Parallel
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 160°C (130 - 320°F)
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 160°C (130 - 320°F)
Thermal Conductivity
Thermal Conductivity
Specific Heat
Vicat Softening Temperature
10N, 50°C/h
50N, 50°C/h
Hot Ball Pressure Test
Plate 3mm
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
DIN 51046
ISO 306
VDE 0470
|
℃(℉)
℃(℉)
E-4/C (E-4/F)
E-4/C (E-4/F)
2
W/m K (Btu in/h ft F)
2
W/m K (Btu in/h ft F)
J/kg K (Btu/lb F)
℃(℉)
℃(℉)
|
115 (239)
180 (356)
50 (122)
60 (140)
225 (437)
0.72 (0.4)
1.3 (0.72)
1.8 (1.0)
0.9 (0.5)
1.3 (0.72)
1.62 (0.9)
0.25 (1.7)
0.25 (1.7)
2090 (0.5)
215 (420)
175 (350)
180 (356)
|
|
Rheological
Melt Volume-Flow Rate
|
ISO 1133
|
3
cm /10 min (ml/10 min)
|
10
|
|
Property
|
Test Method
|
Units
|
Value
|
|
Other
Density
Ball Indentation Hardness
H 358/30
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 2039-1
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m (g/cm )
MPa (kpsi)
%
%
|
1300 (1.30)
139 (20)
0.2
0.4
1.5
1.7
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
Hold Pressure Time
Snake Flow
90MPa, 5x0.30mm
90MPa, 5x0.50mm
90MPa, 5x0.75mm
90MPa, 5x1.00mm
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
s/mm (s/in)
mm (in)
|
240-260 (465-500)
250 (480)
30-130 (85-265)
80 (175)
2-4
110-130 (230-265)
<0.04
3-4 (75-100)
8 (0.3)
26 (1)
60 (2.4)
95 (3.7)
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm. Test temperatures are 23°C unless otherwise stated.