LNP STAT-KON* POLYAMIDES COMPOUND
TOUGH, TAILORED ELECTRICAL PROPERTIES
Polyamide-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound PA66 RD000IXP 塑料数据物性表
Also known as:LNP™ Stat-kon™ Compound R-1 HI
Product reorder name:RD000IXP
LNP STAT-KON* RD000IXP is a compound based on Nylon 66 resin containing Carbon Powder. Added features of this material include: Electrically Conductive.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,5mm/min | 550 | kgf/cm² | ASTM D 638 |
Tensile Stress,brk,Type I,5mm/min | 540 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,5mm/min | 12 | % | ASTM D 638 |
Tensile Strain,brk,Type I,5mm/min | 12.2 | % | ASTM D 638 |
Tensile Modulus,50mm/min | 27400 | kgf/cm² | ASTM D 638 |
Flexural Modulus,1.3mm/min,50mm span | 25300 | kgf/cm² | ASTM D 790 |
Tensile Stress,yield,5mm/min | 51 | MPa | ISO 527 |
Tensile Stress,break,5mm/min | 50 | MPa | ISO 527 |
Tensile Strain,yield,5mm/min | 14.3 | % | ISO 527 |
Tensile Strain,break,5mm/min | 14.6 | % | ISO 527 |
Tensile Modulus,1mm/min | 2230 | MPa | ISO 527 |
Flexural Stress | 83 | MPa | ISO 178 |
Flexural Modulus,2mm/min | 2590 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 108 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 7 | cm-kgf/cm | ASTM D 256 |
Multiaxial Impact | 224 | cm-kgf | ISO 6603 |
Instrumented Impact Total Energy,23℃ | 101 | cm-kgf | ASTM D 3763 |
Izod Impact,unnotched 80*10*4 +23℃ | 111 | kJ/m² | ISO 180/1U |
Izod Impact,notched 80*10*4 +23℃ | 9 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
HDT,0.45 MPa,3.2mm,unannealed | 216 | ℃ | ASTM D 648 |
HDT,1.82 MPa,3.2mm,unannealed | 71 | ℃ | ASTM D 648 |
CTE,-30℃ to 30℃,flow | 8.87E-05 | 1/℃ | ASTM D 696 |
CTE,-30℃ to 30℃,xflow | 8.71E-05 | 1/℃ | ASTM D 696 |
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 190 | ℃ | ISO 75/Bf |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 65 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Density | 1.19 | g/cm³ | ASTM D 792 |
Moisture Absorption,50% RH,24 hrs | 0.63 | % | ASTM D 570 |
Mold Shrinkage,flow,24 hrs(5) | 2-3 | % | ASTM D 955 |
Mold Shrinkage,xflow,24 hrs(5) | 2-3 | % | ASTM D 955 |
Mold Shrinkage,flow,24 hrs(5) | 2.92 | % | ISO 294 |
Mold Shrinkage,xflow,24 hrs(5) | 3.17 | % | ISO 294 |
Density | 1.18 | g/cm³ | ISO 1183 |
Moisture Absorption(23℃/50% RH) | 0.63 | % | ISO 62 |
ELECTRICAL | Value | Unit | Standard |
Surface Resistivity | 2.E+00-6.E+00 | Ohm | ASTM D 257 |
Source GMD,last updated:2009/04/16 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 80 | ℃ |
Drying Time | 4 | hrs |
Maximum Moisture Content | 0.15-0.25 | % |
Melt Temperature | 280-305 | ℃ |
Front-Zone 3 Temperature | 295-305 | ℃ |
Middle-Zone 2 Temperature | 280-295 | ℃ |
Rear-Zone 1 Temperature | 265-275 | ℃ |
Mold Temperature | 95-110 | ℃ |
Back Pressure | 0.2-0.3 | MPa |
Screw Speed | 30-60 | rpm |
Source GMD,last updated:2009/04/16 |