- 产 品：PA66 RF206 含有玻璃纤维和专有的润滑剂
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP LUBRILOY* POLYAMIDES COMPOUND
TOUGH & STRONG -- WITH UNIQUE LUBRICITY
Polyamide-based LNP Lubriloy compounds provide enhanced lubrication through a unique, patented lubrication technology.
LNP™ LUBRILOY™ Compound PA66 RF206 塑料物性表
Also known as:LNP™ Lubriloy™ Compound RF-30
Product reorder name:RF206
LNP LUBRILOY* RF206 is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant, Added features of this material includes: Internally Lubricated
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,brk,Type I,5mm/min | 1230 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 2.5 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 89400 | kgf/cm² | ASTM D 638 |
| Flexural Stress,brk,1.3mm/min,50mm span | 1760 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 71900 | kgf/cm² | ASTM D 790 |
| Tensile Stress,break,5mm/min | 118 | MPa | ISO 527 |
| Tensile Strain,break,5mm/min | 2.3 | % | ISO 527 |
| Tensile Modulus,1mm/min | 8460 | MPa | ISO 527 |
| Flexural Stress | 167 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 7200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 70 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 11 | cm-kgf/cm | ASTM D 256 |
| Multiaxial Impact | 37 | cm-kgf | ISO 6603 |
| Instrumented Impact Total Energy,23℃ | 135 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*4 +23℃ | 35 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 9 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 258 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 241 | ℃ | ASTM D 648 |
| CTE,-30℃ to 30℃,flow | 3.80E-05 | 1/℃ | ASTM D 696 |
| CTE,-30℃ to 30℃,xflow | 7.50E-05 | 1/℃ | ASTM D 696 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 252 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 224 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.24 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.38 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 0.6 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 1.2 | % | ASTM D 955 |
| Wear Factor Washer | 45 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.4 | - | ASTM D 3702 Modified |
| Static COF | 0.4 | - | ASTM D 3702 Modified |
| Moisture Absorption(23℃/50% RH) | 0.66 | % | ISO 62 |
| Source GMD,last updated:2012/12/06 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15-0.25 | % |
| Melt Temperature | 270-280 | ℃ |
| Front-Zone 3 Temperature | 295-305 | ℃ |
| Middle-Zone 2 Temperature | 280-295 | ℃ |
| Rear-Zone 1 Temperature | 265-275 | ℃ |
| Mold Temperature | 80-95 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2012/12/06 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【LNP™ LUBRILOY™ Compound PA66 RF206】