PA66 RFL46ES 含玻璃纤维,聚四氟乙烯,热稳定,易成型
  • 产 品:PA66 RFL46ES 含玻璃纤维,聚四氟乙烯,热稳定,易成型
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP* Lubricomp* Compound
LNP Lubricomp Resin All Series
LNP* Lubricomp* compounds provide improved wear resistance and lower friction by combining engineering resins with internal lubricants. Lubricomp compounds, which can also be stiffened with glass or other fiber, can help extend product life and reduce or eliminate squeaks and other noise from moving parts. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ Lubricomp™ Compound PA66 RFL46ES 塑料数据

Also known as:LNP™ Lubricomp™ Compound RFL-4046 EM HS BK8-115
Product reorder name:RFL46ES
LNP* Lubricomp* RFL46ES is a compound based on Nylon 6/6 containing Glass Fiber and PTFE. Characteristics are: Internally Lubricated, Heat Stabilized and Easy Molding.

MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 1480 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 2.6 % ASTM D 638
Tensile Modulus,50mm/min 110900 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 2270 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 94600 kgf/cm² ASTM D 790
Tensile Stress,break,5mm/min 145 MPa ISO 527
Tensile Strain,break,5mm/min 2.6 % ISO 527
Tensile Modulus,1mm/min 10420 MPa ISO 527
Flexural Stress 221 MPa ISO 178
Flexural Modulus,2mm/min 9260 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 95 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 9 cm-kgf/cm ASTM D 256
Multiaxial Impact 29 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 86 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 56 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 9 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 251 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 233 ASTM D 648
CTE,-30℃ to 30℃,flow 3.10E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 8.40E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 251 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 232 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.55 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.43 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.2-0.5 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.9-3 % ASTM D 955
Wear Factor Washer 12 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Wear Factor Ring 0 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.59 - ASTM D 3702 Modified
Static COF 0.63 - ASTM D 3702 Modified
Moisture Absorption(23℃/50% RH) 0.82 % ISO 62
Source GMD,last updated:2009/09/18
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 280-305
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2009/09/18

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™ Lubricomp™ Compound PA66 RFL46ES