- 产 品：PA66 103FHS NC010 热稳定,润滑,快速周期
- 产 地：DuPont 杜邦
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Unreinforced Resins
非增强树脂
Zytel® 103FHS NC010 is a heat stabilized, internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.
zytel®103FHS NC010是一种热稳定，内部润滑聚酰胺66树脂注塑。它是为快速周期和高生产率。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66
>PA66<
|
|
|
Mechanical
Yield Stress
Nominal Strain at Break
Yield Strain
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
85(12.3)
20
4.5
3100(450)
2800(410)
4.5
5.5
350
NB
|
55(8.0)
>100
25
1400(200)
1300(190)
3
11
NB
NB
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
23-55℃(73-130℉)
CLTE, Parallel
23-55℃(73-130℉)
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
200(392)
70(158)
262(504)
1.1(0.61)
1.0(0.55)
|
|
|
Electrical
CTI
CTI
3.0mm
|
IEC 60112
UL 746A
|
V
V
|
600
600
|
|
|
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
Oxygen Index
Glow Wire Flammability Index
0.71mm
1.5mm
3.0mm
Glow Wire Ignition Temperature
0.71mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
IEC 60695-2-12
IEC 60695-2-13
|
%
℃
℃
|
V-2
V-2
28
850
960
960
725
725
725
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Flammability
High Amperage Arc Ignition Resistance
0.71mm
1.5mm
3.0mm
Hot Wire Ignition
0.71mm
1.5mm
3.0mm
|
UL 746A
UL 746A
|
arcs
s
|
200
>200
>200
9
11
24
|
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
1.5mm
RTI, Strength
0.71mm
1.5mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
|
140
95
110
115
125
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
Mold Shrinkage
Flow, 1.6mm(0.063in)
Flow, 3.2mm(0.126in)
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
%
|
1140(1.14)
2.6
8.5
1.3
1.4
1.4
1.8
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-300(535-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2005.