- 产 品:PA66 BM70G15HSLR BK537 玻璃纤维15%增强
- 产 地:DuPont 杜邦
- 价 格:电话报价
- 库 存:20吨
- 交 货:江苏苏州
- 苏州希普能:185 5121 3137 谭经理
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Blow Moldable Resins
吹塑成形树脂
Zytel® BM70G15HSLR BK537 is a 15% glass fiber reinforced polyamide 66 for blow molding.
zytel的®BM70G15HSLR BK537是15%玻璃纤维增强聚酰胺66吹塑。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66-IGF15
>PA66-IGF15<
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Notched Charpy Impact Strength
Unnotched Charpy Impact Strength
|
ISO 527
ISO 527
ISO 527
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
MPa (kpsi)
2
kJ/m
2
kJ/m
|
110 (16.0)
4.5
5400 (783)
14
71
|
60 (8.7)
21
3500 (510)
14
71
|
Thermal
Deflection Temperature
1.80MPa
Melting Temperature
10°C/min
|
ISO 75-1/-2
ISO 11357-1/-3
|
℃(℉)
℃(℉)
|
228 (442)
263 (505)
|
|
Other
Density
Molding Shrinkage
Parallel
|
ISO 1183
ISO 294-4
|
3 3
kg/m (g/cm )
%
|
1250 (1.25)
0.39
|
|
Processing - Blow Molding
Melt Temperature Range
Melt Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
Swell Ratio
|
|
℃(℉)
℃(℉)
h
℃(℉)
%
|
285-305 (545-580)
290 (555)
4-5
100-110 (212-230)
<0.05
1.6
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The above data are preliminary and are subject to change as additional data are developed on subsequent lots.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2008