DuPont™ Minlon® 数据
杜邦™minlon® 数据
Low Warp Resins
低翘曲树脂
Minlon ® 10B40 NC010 is a 40% mineral reinforced polyamide 66 resin for injection molding.
minlon®10B40 NC010是40%矿物增强聚酰胺66树脂注塑。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
PA66-MD40
>PA66-MD40<
|
||
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Poisson's Ratio
Flexural Modulus
Notched Charpy Impact Strength
-40°C (-40°F)
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa (kpsi)
%
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
|
92 (13.3)
2.5
9600 (1400)
0.41
9000 (1300)
2
2
3
18
25
|
58 (8.4)
8
5400 (785)
4800 (700)
2
2
3
17
40
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 160°C (130 - 320°F)
CLTE, Parallel
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 160°C (130 - 320°F)
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
|
245 (473)
205 (401)
263 (505)
0.53 (0.29)
0.66 (0.36)
1.1 (0.61)
0.33 (0.18)
0.36 (0.20)
0.39 (0.22)
|
|
Electrical
CTI
3.0mm
|
UL 746A
|
V
|
>600
|
|
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
Oxygen Index
High Amperage Arc Ignition Resistance
0.75mm
1.5mm
3.0mm
Hot Wire Ignition
0.75mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
UL 746A
UL 746A
|
%
arcs
s
|
HB
HB
23
>200
>200
>200
8
8
10
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Temperature Index
RTI, Electrical
0.71mm
1.5mm
RTI, Impact
0.71mm
1.5mm
3.0mm
RTI, Strength
0.71mm
1.5mm
|
UL 746B
UL 746B
UL 746B
|
°C
°C
°C
|
105
120
65
105
115
65
115
|
|
Other
Density
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
Mold Shrinkage
Flow, 1.6mm (0.062in)
Flow, 3.2mm (0.126in)
Flow, 6.4mm (0.25in)
Transverse, 1.6mm (0.062in)
Transverse, 3.2mm (0.126in)
Transverse, 6.4mm (0.25in)
|
ISO 1183
ISO 294-4
|
3 3
kg/m (g/cm )
%
%
|
1510 (1.51)
0.9
0.5
0.4
0.4
0.6
0.9
0.9
1.2
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
|
285-305 (545-580)
295 (560)
70-120 (160-250)
100 (210)
2-4
80 (175)
<0.20
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Minlon® are trademarks or registered trademarks of DuPont Company. Copyright© 2005.