PA66 22C NC010 矿物/玻纤38%增强,热稳定
  • 产 品:PA66 22C NC010 矿物/玻纤38%增强,热稳定
  • 产 地:DuPont 杜邦
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

DuPont™ Minlon® 数据
杜邦™minlon® 数据
mineral reinforced nylon resin
矿物增强尼龙树脂

Minlon ® 22C NC010 is a 38% mineral/glass reinforced, heat stabilized polyamide 66 resin for injection molding.
minlon®22C NC010 是38%矿物/玻璃纤维增强,热稳定聚酰胺66树脂注塑成型。

Property
Test Method
Value
Units
DAM            50%RH
Identification
Resin Identification
Part Marking Code
ISO 1043
ISO 11469
PA66-(MD+GF)38
>PA66-(MD+GF)38<
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-40°C (-40°F)
-30°C (-22°F)
23°C (73°F)
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
MPa (kpsi)
%
MPa (kpsi)
MPa (kpsi)
2
kJ/m
2
kJ/m
130 (18.9)
3.5
7500 (1090)
6500 (940)
3
3
4
40
50
82 (11.9)
10
5000 (725)
5000 (725)
3
4
6
35
45

Property
Test Method
Units
Value
DAM
50%RH
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10°C/min
CLTE, Normal
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 160°C (130 - 320°F)
CLTE, Parallel
-40 - 23°C (-40 - 73°F)
23 - 55°C (73 - 130°F)
55 - 160°C (130 - 320°F)
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
°C (°F)
°C (°F)
E-4/C (E-4/F)
E-4/C (E-4/F)
255 (491)
230 (446)
263 (505)
0.53 (0.29)
0.62 (0.33)
1.0 (0.56)
0.39 (0.22)
0.41 (0.23)
0.36 (0.20)
 
Electrical
Relative Permittivity
1E2 Hz
1E6 Hz
Volume Resistivity
Dissipation Factor
1E2 Hz
1E6 Hz
Electric Strength
2.0mm
CTI
3.0mm
IEC 60250
IEC 60093
IEC 60250
IEC 60243-1
UL 746A
ohm m
E-4
kV/mm (V/mil)
V
4
4
1E11
100
100
20 (510)
475
7
4
1E7
200
500
18 (460)

Property
Test Method
Units
Value
DAM
50%RH
Flammability
Flammability Classification
0.81mm
Flammability Classification
0.81mm
Oxygen Index
High Amperage Arc Ignition Resistance
1.5mm
3.0mm
Hot Wire Ignition
1.5mm
3.0mm
IEC 60695-11-10
UL94
ISO 4589-1/-2
UL 746A
UL 746A
%
arcs
s
HB
HB
24
>200
>200
117
120
 
Temperature Index
RTI, Electrical
0.81mm
RTI, Impact
0.81mm
RTI, Strength
0.81mm
UL 746B
UL 746B
UL 746B
°C
°C
°C
65
65
65
 
Other
Density
Water Absorption
Equilibrium 50%RH
Immersion 24h, 2.0mm
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
ISO 1183
ISO 62, Similar to
ISO 294-4
3      3
kg/m (g/cm )
%
%
1450 (1.45)
1.4
1.0
5.4
0.9
0.7
 

Property
Test Method
Units
Value
DAM
50%RH
Other
Mold Shrinkage
Flow, 1.6mm (0.062in)
Flow, 3.2mm (0.126in)
Flow, 6.4mm (0.25in)
Transverse, 1.6mm (0.062in)
Transverse, 3.2mm (0.126in)
Transverse, 6.4mm (0.25in)
 
%
0.6
0.7
0.8
0.8
0.9
1.1
 
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
 
°C (°F)
°C (°F)
°C (°F)
°C (°F)
h
°C (°F)
%
285-305 (545-580)
295 (560)
70-120 (160-250)
100 (210)
2-4
80 (175)
<0.20
 

Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23°C unless otherwise stated.

The DuPont Oval Logo, DuPont™, The miracles of science™ and Minlon® are trademarks or registered trademarks of DuPont Company. Copyright© 2005.