DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Unreinforced Resins
非增强树脂
Zytel® 135F NC010 is a nucleated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.
zytel®135F NC010是一个有核的聚酰胺66树脂注塑。它是为快速周期和高生产率。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA66
>PA66<
|
|
Mechanical
Yield Stress
Strain at Break
50mm/min
Nominal Strain at Break
Yield Strain
Tensile Modulus
Tensile Creep Modulus
1h
1000h
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 527
ISO 899
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
%
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
96(13.9)
20
13
4.5
3600(522)
3
4
NB
NB
|
67(9.7)
>50
50
18
2000(290)
2000(290)
1280(186)
2.5
9
NB
NB
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
23-55℃(73-130℉)
CLTE, Parallel
23-55℃(73-130℉)
Vicat Softening Temperature
50N
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
℃(℉)
|
210(410)
75(167)
263(505)
1.21(0.68)
1.21(0.68)
243(469)
|
|
Electrical
Relative Permittivity
1E2 Hz
1E6 Hz
Dissipation Factor
1E2 Hz
1E6 Hz
CTI
CTI
3.0mm
|
IEC 60250
IEC 60250
IEC 60112
UL 746A
|
E-4
V
V
|
3.9
3.8
70
200
600
>600
|
8.7
3.9
2400
600
|
Flammability
Flammability Classification
0.71mm
Flammability Classification
0.71mm
|
IEC 60695-11-10
UL94
|
|
V-2
V-2
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Flammability
Glow Wire Flammability Index
0.71mm
1.5mm
3.0mm
Glow Wire Ignition Temperature
0.71mm
1.5mm
3.0mm
|
IEC 60695-2-12
IEC 60695-2-13
|
℃
℃
|
960
960
960
725
750
800
|
|
Temperature Index
RTI, Electrical
0.71mm
RTI, Impact
0.71mm
RTI, Strength
0.71mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
130
75
85
|
|
Other
Density
Hardness, Rockwell
Scale M
Scale R
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Parallel, 2.0mm
|
ISO 1183
ISO 2039/2
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1140(1.14)
87
123
2.7
8.5
0.7
|
64
116
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-300(535-570)
290(555)
50-90(120-190)
70(160)
2-4
80(175)
<0.20
|
|
PA66 美国杜邦 FR52G35BL
PA66 美国杜邦 FR52G45BL
PA66 美国杜邦 FR530 NC010
PA66 美国杜邦 FR53G50HSLR
PA66 美国杜邦 FR7025V0F
PA66 美国杜邦 FR7025V0F NC010
PA66 美国杜邦 FR70M30 VO
PA66 美国杜邦 FR70M30V0
PA66 美国杜邦 FR72G25
PA66 美国杜邦 FR72G25 V0
PA66 美国杜邦 FR72G25V0 NC010
PA66 美国杜邦 HTN 501
PA66 美国杜邦 HTN 502
PA66 美国杜邦 HTN150002
PA66 美国杜邦 HTN51G15HSIL
PA66 美国杜邦 HTN51G35HSL
PA66 美国杜邦 HTN51G35HSL BK083
PA66 美国杜邦 HTN52G30BL
PA66 美国杜邦 HTN52G30NH
PA66 美国杜邦 HTN52G35HSL
PA66 美国杜邦 HTN52G35HSL NC010
PA66 美国杜邦 HTN52G45HSL
诚信经营 质量保证 原厂原包 销售热线:18551213137 谭先生 网址:www.pa66-suliao.com