- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：PA610 QEP35M 含有碳纤维和PTFE/硅树脂
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP™ STAT-KON™ Compound PA610 QEP35M
LNP Stat-Kon QCL-4535 M is a compound based on Nylon 6/10 resin containing carbon fiber and PTFE/Silicone.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5mm/min | 1210 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5mm/min | 1210 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5mm/min | 1.5 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 1.5 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 236300 | kgf/cm² | ASTM D 638 |
| Flexural Stress,brk,1.3mm/min,50mm span | 2180 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 93300 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,5mm/min | 140 | MPa | ISO 527 |
| Tensile Stress,break,5mm/min | 140 | MPa | ISO 527 |
| Tensile Strain,yield,5mm/min | 2.5 | % | ISO 527 |
| Tensile Strain,break,5mm/min | 2.6 | % | ISO 527 |
| Tensile Modulus,1mm/min | 13430 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 205 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 9810 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 73 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 6 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,unnotched 80*10*4 +23℃ | 40 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 219 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 201 | ℃ | ASTM D 648 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 219 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 229 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.31 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.27 | % | ASTM D 570 |
| Mold Shrinkage,flow,24 hrs(5) | 0.4-0.4 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 0.7-1 | % | ASTM D 955 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Moisture Absorption(23℃/50% RH) | 0.4 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+00-3.E+00 | Ohm | ASTM D 257 |
| Source GMD,last updated:2008/03/26 | |||
| parameter lnjection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.12-0.2 | % |
| Melt Temperature | 270-275 | ℃ |
| Front-Zone 3 Temperature | 270-280 | ℃ |
| Middle-Zone 2 Temperature | 260-270 | ℃ |
| Rear-Zone 1 Temperature | 250-260 | ℃ |
| Mold Temperature | 80-95 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2008/03/26 | ||